Modified asphalt binders are still considered important in asphalt pavement. However, the comprehensive use of various modifiers is limited due to storage stability issues. Moreover, there is a scarcity of detailed analyses regarding the degree of separation for asphalt binders among each method despite the utilization of various methods to assess the storage stability of binders. Therefore, a comprehensive analysis was conducted to assess the storage stability of asphalt binder modified with a crumb rubber modifier (CRM) and styrene-isoprene-styrene (SIS), utilizing five evaluation factors following the ASTM D7173 guidelines based on four mixing methods (A: high-shear mixing method, B: low-speed agitating method, C: high-shear mixing method + low mixing method, D: low-speed agitating method + low mixing method). To produce the modified asphalt binder, the proportions of the CRM were 5% and 10% for each binder, and 10% SIS was added to all binders. The results in this study convey that (1) the addition of the modifier led to an increase in G*/sin δ with different mixing methods, but using mixing methods (C and D) for a relatively long time resulted in a lower G*/sin δ, indicating suboptimal performance; (2) through the multiple stress creep recovery (MSCR), rheological properties of Jnr and % rec exhibited trends similar to G*/sin δ evaluation, highlighting an improved elastic recovery with a higher modifier content; (3) storage stability assessment revealed consistent trends in high-shear mixing groups (A and C), while low-speed mixing groups (B and D) exhibited an elevated separation index (SI), suggesting a sensitivity to modification conditions; (4) evaluation using the MSCR method indicated that % rec with a 3.2 kPa load is effective for the sensitive assessment of binder storage stability and Jnr showed a limited sensitivity across varying loads, advocating for % rec for precise evaluation; and (5) despite permitting various tests, achieving consistent results remains challenging. Future research should explore diverse modifiers and optimal evaluation methods to enhance knowledge of binder behavior and separation dynamics.
RESUMO
This study aimed to evaluate the impact of a two-step modification process involving kaolinite and cloisite Na+ on the storage stability of rubberized binders. The process involved the manual combination of virgin binder PG 64-22 with crumb rubber modifier (CRM), which was heated to condition it. The preconditioned rubberized binder was then modified for two hours at a high speed of 8000 rpm using wet mixing. The second stage modification was performed in two parts, with part 1 using only crumb rubber as the modifier and part 2 involving the use of kaolinite and montmorillonite nano clays at a replacement percentage of 3% to the original weight of the binder along with the crumb rubber modifier. The Superpave and multiple shear creep recovery (MSCR) test methods were used to calculate the performance characteristics and separation index % of each modified binder. The results showed that the viscosity properties of kaolinite and montmorillonite improved the performance class of the binder, with montmorillonite demonstrating greater viscosity values than kaolinite even at high temperatures. Additionally, kaolinite with rubberized binders showed higher resistance to rutting, and the % recovery value from multiple shear creep recovery testing indicated that kaolinite with rubberized binders was more effective than montmorillonite with rubberized binders, even at higher load cycles. The use of kaolinite and montmorillonite reduced phase separation between the asphaltene phase and rubber-rich phase at higher temperatures, but the performance of the rubber binder was affected by higher temperatures. Overall, kaolinite with the rubber binder generally demonstrated greater binder performance.
RESUMO
Crumb rubber modifier (CRM) binders easily suffer from instability at high temperatures, with many suggestions being developed to evaluate their storage stability. However, much uncertainty around CRM binders still exists regarding the relationship between mixing methods and experiments in order to calculate the separation index. In this study, a laboratory investigation into how CRM binders behave regarding storage stability using different mixing methods and experiments was conducted. The CRM asphalt binder in this study was prepared through a wet mixing process with the addition of 5% and 10% crumb rubber modifier (by weight) at 200 °C. The three main modification methods were method A: high-shear mixing (8000 rpm) for 2 h, method B: low mixing (300 rpm) for 8 h, and method C: high-shear mixing (8000 rpm) for 2 h + low mixing (300 rpm) for 6 h. In addition, the effect of separation index (SI) on storage stability was assessed, measuring viscosity, G*/sin δ, and percentage recovery. In general, the results of this study revealed that method C appeared to have the most prominent effect on decreasing the difference between the values of the top and bottom parts; the results for 5% CRM using method C showed that there were no differences among the values for the top, middle, and bottom parts; from the MSCR test, method C was effective in decreasing the difference between the values of the top and bottom parts. It was observed that method C improved storage stability. However, the results for percentage recovery were relatively higher than the separation index when using rotational viscosity and G*/sin δ.
RESUMO
The study presents an experimental evaluation to improve the resistivity of binders with "Styrene-Butadiene-Styrene" (SBS) and "Processed oil" by studying the physical properties, rheology, and cracking. For this experiment, PG 64-22 was mixed with SBS at different percentages of 5%, 10%, and 15% by weight of the original binder with two processed oil contents of 6% and 12% by weight of the binder. Laboratory tests have been conducted at various high, medium, and low temperature ranges to evaluate their properties. The processed oil polymer modified asphalt (PMA) binder is artificially aged in both the short and long-term using a Rolling Thin Film Oven (RTFO) and a Pressure Aging Vessel (PAV). The Superpave testing method was performed on modified binders using a Rotational Viscometer (RV), Dynamic Shear Rheometer (DSR), and Bending Beam Rheometer (BBR). The results of this study illustrate (1) The addition of SBS leads to higher viscosity, but the co-modification of asphalt binder with the processed oil shows a significant modulation of the viscosity value. (2) In addition, processed oil reduced the resistance to rutting, but the addition of SBS significantly improved the rutting resistance of the asphalt binder. (3) The addition of SBS and processed oil improved the value of G sin δ, notably. (4) According to BBR, it has been shown that the addition of SBS in addition to the processed oil improves the stiffness values of modified asphalt binders.
RESUMO
This study investigates the effectiveness of processed oil in the modification of PG 64-22 and PG 76-22 by assessing their physical and rheological properties, and multiple comparison was conducted between the two binders. The base binders PG 64-22 and PG 76-22 were blended with processed oil at four different percentages of contents (3%, 6%, 9% and 12% by the weight of the binder) and compared with the control binder in each test. The base and modified binders were artificially short-term and long-term aged using a rolling thin film oven (RTFO) and pressure aging vessel (PAV) procedures. Superpave binder tests were performed on the modified binders by applying a rotational viscometer (RV), dynamic shear rheometer (DSR), and bending beam rheometer (BBR). The comparisons and results presented in this study indicate that (1) the processed oil has a significant effect on the binders' viscosity, which changes with respect to the increment of processed oil content. The viscosity of both modified binders decreased with the addition of 3, 6, 9 and 12% processed oil; (2) the performed DSR test showed that the addition of processed oil had a negative effect on the rutting resistance for both binders, since in PG 64-22, G*/Sin δ values decreased by 55, 65, 75 and 83% with the addition of 3, 6, 9 and 12% processed oil, respectively, while a decrement of G*/Sin δ of 24, 45, 58 and 65% with the addition of 3, 6, 9 and 12% processed oil was observed in PG 76-22; meanwhile, the fatigue cracking performance was improved and was found to be effective, while G* Sin δ in PG76-22 decreased by 9, 30, 36, and 52% and in PG 64-22 by 27, 44, 53, and 67% with the addition of 3, 6, 9 and 12% processed oil; (3) the results from the BBR test indicate significant improvement in the thermal cracking properties of the binders. The addition of 3, 6, 9 and 12% processed oil resulted in a decrease in the stiffness of both the PG 64-22 and PG 76-22 binders, with a positive effect consequently being observed on the m-values of the binders.
RESUMO
Crumb rubber binder with thermoplastic polyurethane (TPU) has been experimented with to characterize the performance properties considering the workability, rutting, fatigue cracking and cracking resistance at low temperatures depending on the temperatures and aging states. Physical and rheological properties were evaluated to proceed with the study by applying Superpave asphalt binder testing and multi-stress creep recovery (MSCR). Based on the targeted experiments, the binder samples were produced at three aging states (original, short-term aged and long-term aged) using a rolling thin film oven (RTFO) and pressure aging vessel (PAV). The results revealed that (i) the addition of TPU into CRM binders has a potential effect on increasing viscoelasticity at the original condition, (ii) CRM binders containing TPU showed improved anti-aging performance based on results of RTFO residues and (iii) the inclusion of TPU made it possible for CRM asphalt binder to improve its fatigue and cracking resistance at low temperature.
RESUMO
The study describes the laboratory assessment (physical and rheological properties) of the binders (PG 64-22 and PG 76-22) modified with Styrene Butadiene Rubber (SBR), and a comprehensive comparison between these two modified binder types. PG 64-22 and PG 76-22 were used as base binders. Both of the base binders were blended with SBR at four different percentages of content (0%, 4%, 6%, and 8% by the weight of the binder). The base and modified binders were artificially short-term and long-term aged using a rolling thin film oven (RTFO) and pressure aging vessel (PAV) procedures. Superpave binder tests were conducted on the SBR modified binder using rotational viscometer (RV), dynamic shear rheometer (DSR), and bending beam rheometer (BBR). In depth rutting performance was investigated using Multiple Stress Creep Recovery (MSCR). The results of this study indicated that (1) the addition of SBR into both binders increased the viscosity and polymer modified asphalt (PMA) binders observed to have more significant effect on its viscosity property; (2) the higher the SBR content, the better the rutting resistance of the binder and it is observed that the effect is prominent on the control binder; (3) MSCR test results showed that the SBR modified binders improved the binder percentage recovery and found to have a more significant effect on the PG 76-22 binder compared to PG 64-22; and (4) both the control PG 64-22 and PMA PG 76-22 binders resulted in similar trends on the cracking properties and were found to have insignificant effects due to the addition of an SBR modifier.
RESUMO
The engineering properties of asphalt binders depend on the types and amounts of additives. However, measuring engineering properties is time-consuming, requires technical expertise, specialized equipment, and effort. This study develops a deep regression model for predicting the engineering property of asphalt binders based on analysis of atomic force microscopy (AFM) image analysis to test the feasibility of replacing traditional measuring estimate techniques. The base asphalt binder PG 64-22 and styrene-isoprene-styrene (SIS) modifier were blended with four different polymer additive contents (0%, 5%, 10%, and 15%) and then tested with a dynamic shear rheometer (DSR) to evaluate the rheological data, which indicate the rutting properties of the asphalt binders. Different deep regression models are trained for predicting engineering property using AFM images of SIS binders. The mean absolute percentage error is decisive for the selection of the best deep regression architecture. This study's results indicate the deep regression architecture is found to be effective in predicting the G*/sin δ value after the training and validation process. The deep regression model can be an alternative way to measure the asphalt binder's engineering property quickly. This study would encourage applying a deep regression model for predicting the engineering properties of the asphalt binder.
RESUMO
Halobacterium salinarum is an extremely halophilic archaea, which is able to live in highly saline environments. In a recent study, several halophilic archaea were found to have the ability to biodegrade organic hydrocarbon pollutants, but protein information regarding hydrocarbon degradation and tolerance in halophilic archaea has been relatively rare. In this study, the protein expression profile of H. salinarum cultured under different diesel concentrations (0, 2 and 4%) was investigated by two-dimensional gel electrophoresis. Proteins which increased their expression levels in diesel media were identified using matrix-assisted laser desorption/ionization-time of flight and electrospray ionization-tandem mass spectrometry analysis. Among these, a protein spot (named D3UPCA) which was up-regulated about nine-fold and found to have COG3388, an uncharacterized protein conserved in archaea, was selected in order to further characterize its functions. The D3UPCA coding gene (named d3upca) was cloned and expressed in Escherichia coli, and purified by the glutathione-S-transferase-fusion method. The function of the protein was estimated using various bioinformatics tools and was predicted to be related to the regulation of transcription and/or translation of genes needed to tolerate stresses associated within the presence of diesel oil.