RESUMO
Fretting-corrosion is one of the failure processes in many applications, including biomedical implants. For example, the modern design of hip implants with multiple components offers better flexibility and inventory storage. However, it will trigger the fretting at the implant interfaces with a small displacement amplitude (< 5 µm) and usually in a partial slip region. Although many studies have been reported on the fretting, they have high displacement amplitude and are in the gross slip region. It is imperative to have an apparatus to overcome such limitations, specifically for hip implant applications. Therefore, this study describes the development of a fretting-corrosion apparatus with low micro-motion (≤ 5 µm) that can simultaneously monitor the corrosion process. Initial experiments with Ti6Al4V-Ti6Al4V in 0.9% saline, Ti6Al4V-Ti6Al4V in bovine calf serum (BCS), and ZrO2-Ti6Al4V in BCS were conducted to validate the system. As a result, the fretting regime of all groups remained partially slip region throughout the 3600 cycles, and the possible failure mechanisms are proposed in this manuscript.
RESUMO
Background: The Lane plate was one of the first widely used bone plates, utilized in the first decades of the twentieth century. Here we present the results of a retrieval analysis on a Lane plate, and a review of the history of these plates. Our patient underwent plating of her femur with a Lane plate in 1938. She developed a sciatic nerve palsy, managed surgically later that year by Dr. Arthur Steindler at the University of Iowa. Her femur healed, her nerve recovered, and she did well until 2020, at age 94, when she presented to the University of Iowa with a draining sinus that appeared to communicate with the plate. She underwent irrigation and debridement with hardware removal. The plate was sectioned, and its composition and structure characterized. Methods: We retrieved hard copies of the patient's archived medical records from 1938, which document in detail the treatments performed by Dr. Steindler. The plate was analyzed using scanning electron microscopy (SEM) to characterize the surface of the plate. A cross section was taken from the plate, and the composition of the alloy was determined using energy dispersive x-ray spectroscopy (EDS). A review of the literature surrounding early plating techniques was conducted. Results: Our patient recovered from her surgery and soon returned to her baseline state of health. Intraoperative cultures grew C. acnes. Analysis of the surface of the plate demonstrated significant corrosion, and the crystal structure seen on SEM suggested a strong alloy that is prone to corrosion. Analysis of the cross section with EDS demonstrated an alloy containing 94.9% iron, 1.7% aluminum, 1.2% chromium, and 1.1% manganese. Conclusion: The Lane plate was introduced around 1907 by Sir William Arbuthnot Lane, a British surgeon, and was one of the first widely used devices for the plating of fractures. Given that this patient was likely one of the last to be treated with a Lane plate, this may be the final opportunity for such a retrieval analysis. Level of Evidence: IV.
Assuntos
Placas Ósseas , Fraturas Ósseas , Humanos , Feminino , Idoso de 80 Anos ou mais , Ligas , Fêmur , Fixação Interna de FraturasRESUMO
PURPOSE: Heterotopic ossification (HO) formed over the major components and fixation screw heads of an alloplastic temporomandibular joint replacement (TMJR) prosthesis can result in decreased quality of life, limited function, prosthesis failure, and hinder prosthesis revision, replacement, or removal. This study simulated HO removal from the major components and fixation screw heads of alloplastic TMJR prostheses using an erbium, chromium-doped yttrium, scandium, gallium, and garnet (Er,Cr:YSGG) laser and compared the results to conventional methods of HO removal. The surface morphology and chemical structure of the exposed components were analyzed. The investigators hypothesize that HO removal with an Er,Cr:YSGG laser causes less damage to TMJR prosthesis components compared to conventional HO removal methods. METHODS: This multiple test descriptive analysis simulated HO removal from TMJR prostheses mounted to stereolithic models. Simulated HO removal was completed using a novel Er,Cr:YSGG laser method and conventional methods which utilized a fissure carbide bur in a high-speed rotary instrument, a standard osteotome, and an ultrasonic aspirator. Surfaces exposed on the TMJR prostheses were analyzed for morphological or chemical change using scanning electron microscopy, energy dispersive X-ray spectroscopy, and Raman spectroscopy. RESULTS: The Er,Cr:YSGG laser did not adversely affect the titanium screws or titanium components of the TMJR prostheses, while conventional methods of HO removal did. HO removal using the Er,Cr:YSGG laser and conventional methods both inflicted surface damage to the fossa ultrahigh molecular weight polyethylene component of the TMJR prostheses. CONCLUSION: Damage inflicted to titanium alloy or commercially pure titanium components of TMJR prostheses by conventional HO removal methods can be avoided by instead removing HO with an Er,Cr:YSGG laser. However, long exposure of the Er,Cr:YSGG laser to ultrahigh molecular weight polyethylene surfaces should be avoided. Additional research to expand on applications to other procedures and in other surgical fields is encouraged.
Assuntos
Lasers de Estado Sólido , Ossificação Heterotópica , Humanos , Lasers de Estado Sólido/uso terapêutico , Titânio , Qualidade de Vida , Ossificação Heterotópica/cirurgia , Polietilenos , Articulação Temporomandibular/cirurgiaRESUMO
Ti6Al4V is the most common titanium alloy within the biomaterial field. While material standards for different variations of this alloy exist, there are only minimal requirements with respect to its microstructure which is directly related to the alloy's properties. Thus, a better understanding of the Ti6Al4V microstructure of common contemporary implant components and its effect on the electrochemical behavior is needed; including additively manufactured (AM) devices. Therefore, this study aimed at characterizing the microstructures of conventional and AM total joint replacement components, and to identify the effect of microstructure on the electrochemical behavior. Thus, 22 components from conventional (surgically retrieved cast and wrought implants) and AM implants (not previously implanted) were analysed to characterize microstructure by means of electron backscatter diffraction (EBSD) and energy dispersive X-Ray spectroscopy (EDS), and tested to determine its electrochemical behavior (potentiodynamic polarization and EIS). The microstructure of the conventional implants varied broadly but could be categorized into four groups as to their grain size and shape: fine equiaxed, coarse equiaxed, bimodal, and lamellar. The AM components exhibited a fifth category: lath-type. The AM components had a network of ß-phase along the α-phase grain boundaries, prior ß-grains, and manufacturing voids. Finally, the electrochemical study showed that the equiaxed coarse grains and lath-type grains (AM components) had inferior electrochemical behavior, whereas cast alloys had superior electrochemical behaviour; fine-grained wrought alloys likely provide the best compromise between electrochemical and mechanical properties.
RESUMO
PURPOSE: Metallic temporomandibular joint replacement (TMJR) systems vary depending on design, material composition, and manufacturing methods such as casting, forging, and additive manufacturing. Therefore, the purpose of this study was to measure the association between manufacturing process of TMJR systems in terms of microstructure and electrochemical properties. MATERIALS AND METHODS: The sample was composed of new or surgically retrieved TMJ replacement devices of either titanium alloy (Ti6Al4V) or cobalt-chromium-molybdenum (CoCrMo) alloy from 8 different manufacturers. The primary predictor variable was alloy type, according to its manufacturing process (wrought, cast, additively manufactured [AM]). The primary outcome variables were 1) microstructure (grain size, aspect ratio, and phase content) and 2) corrosion potential and current, polarization resistance, and capacitance. Differences between alloy groups were determined by t tests, Kruskal-Wallis, and Mann-Whitney tests. RESULTS: We demonstrated that the TMJR CoCrMo and Ti6Al4V alloy microstructures can vary broadly within American Society for Testing and Materials specifications, where the components made of Ti6Al4V had 3 types of microstructures (equiaxial, bimodal, and martensitic) out of 10 samples, and the components made of CoCrMo had 2 types of microstructure (equiaxial and dendritic) out of 16 samples. Some CoCrMo alloys exhibited preferential corrosion sites, while wrought Ti6Al4V alloys trended toward a superior corrosion behavior (corrosion rate: 2 × 10-9 A/cm2, polarization resistance: 5,000,000 kΩcm2, and capacitance: 10 µSsa/cm2) compared with AM alloys (39 × 10-9 A/cm2, 1676 kΩcm2, 36 µSsa/cm2, respectively), where 4 samples of each group were tested and repeated 5 times. Among four AM devices, two exhibited a significantly inferior corrosion behavior. CONCLUSIONS: Although AM is an exciting emerging new technology that allows manufacturing of custom-made TMJR, their corrosion behavior is still inferior in comparison to that of traditional wrought alloys. Preventing corrosion is crucial because it can cause surface defects that may lead to implant fracture.
Assuntos
Ligas , Prótese Articular , Ligas/química , Animais , Corrosão , Humanos , Teste de Materiais , Camundongos , Propriedades de Superfície , Articulação Temporomandibular/cirurgiaRESUMO
The frequency of surgeries involving the use of metal implants in orthopedic medicine to replace degenerative or fractured joints is increasing, and it is therefore important to optimize the lifespan and quality of these implants. Advances in additive manufacturing (AM), or 3D printing, are creating new opportunities to personalize implants in ways that reduce mechanical stress at the joint implant interface and improve bone ingrowth and implant stability; however, it is not well understood if and to what degree the AM process alters the corrosion behavior of the materials it produces. In this study, six Ti6Al4V prints manufactured via a selective laser melting (SLM) method were examined regarding their corrosion behavior in both saline and bovine calf serum (BCS) solutions. Ecorr and Icorr values were comparable between the CM-Ti6Al4V control and SLM-EDM surfaces; however, SLM surfaces were found to have more narrow passivation behavior evidenced by significant decreases in Epass values relative to CM-Ti6Al4V. We believe this is a consequence of microstructural differences between CM-Ti6Al4V and SLM-Ti6Al4V. Specifically, the SLM-Ti6Al4V demonstrated a dominant α' martensitic microstructure and decreased vanadium-rich ß-phase. BCS solution had a detrimental effect on potential parameters, Ecorr and OCP, decreasing these values relative to their saline counterparts. Increased surface roughness of the SLM-printed surface seemed to amplify the effects of the BCS solution. Furthermore, modest decreases in Epass and Ipass were observed in BCS solution, suggesting that the presence of protein may also interfere with passivation behavior. These findings have implications for how SLM-Ti6Al4V implants will perform in vivo and could possibly influence implant longevity and performance.