Knowledge about the thermodynamic equilibria of the P2O5-Na2O and P2O5-MgO systems is very important for controlling the phosphorus content of steel materials in the process of steelmaking dephosphorization. The phase equilibrium and thermodynamic data of the P2O5-Na2O and P2O5-MgO systems were critically evaluated and re-assessed by the CALPHAD (CAlculation of PHAse Diagram) approach. The liquid phase was described by the ionic two-sublattice model for the first time with the formulas (Na+1)P(O-2, PO3-1, PO4-3, PO5/2)Q and (Mg+2)P(O-2, PO3-1, PO4-3, PO5/2)Q, respectively, and the selection of the species constituting the liquid phase was based on the structure of the phosphate melts. A new and improved self-consistent set of thermodynamic parameters for the P2O5-Na2O and P2O5-MgO systems was finally obtained, and the calculated phase diagram and thermodynamic properties exhibited excellent agreement with the experimental data. The difference in the phase composition of invariant reactions from the experimentally determined values reported in the literature is less than 0.9 mol.%. The present thermodynamic modeling contributes to constructing a multicomponent oxide thermodynamic database in the process of steelmaking dephosphorization.
RESUMO
Phase relations of the Fe-Cr-Er system in the temperature range 973-1273 K were experimentally investigated using equilibrated alloys. The isothermal sections consisted of 9 single-phase regions, 16 two-phase regions, and 8 three-phase regions at 973 K and 1073 K. At 1273 K, the σ phase disappeared, and liquid appeared. All single phases had a solid solubility range that showed a downward trend with a decrease in temperature. The homogeneity range of the ErFe12-xCrx ternary compound was determined to be x = 1.8-4.5. The more accurate phase relations obtained in this work can better guide the preparation of Fe-Cr-Er alloys in actual production.