Chemosphere ; 159: 602-609, 2016 Sep.
Artigo em Inglês | MEDLINE | ID: mdl-27343867

RESUMO

Amphiphilic magnetic composites were produced based on chrysotile mineral and carbon structures by chemical vapor deposition at different temperatures (600-900 °C) and cobalt as catalyst. The materials were characterized by elemental analysis, X-ray diffraction, vibrating sample magnetometry, adsorption and desorption of N2, Raman spectroscopy, scanning electronic microscopy, and thermal analysis showed an effective growth of carbon structures in all temperatures. It was observed that at 800 and 900 °C, a large amount of carbon structures are formed with fewer defects than at 600 and 700 °C, what contributes to their stability. In addition, the materials present magnetic phases that are important for their application as catalysts and adsorbents. The materials have shown to be very active to remove the oil dispersed in a real sample of emulsified wastewater from biodiesel production and to remove methylene blue by adsorption and oxidation via heterogeneous Fenton mechanism.


Assuntos
Asbestos Serpentinas/química , Carbono/química , Eliminação de Resíduos Líquidos/métodos , Águas Residuárias/química , Poluentes Químicos da Água/análise , Adsorção , Catálise , Azul de Metileno/química , Oxirredução , Análise Espectral Raman , Propriedades de Superfície , Difração de Raios X
2.
J Nanosci Nanotechnol ; 12(3): 2661-7, 2012 Mar.
Artigo em Inglês | MEDLINE | ID: mdl-22755105

RESUMO

In this work, it is demonstrated how a novel technique based on temperature-programmed chemical vapor deposition (TPCVD) can be used to investigate the synthesis of carbon nanotubes (CNTs) from methane on a classic catalyst FeMo(x)/MgO (x = 0.07, 0.35 and 1.00). TPCVD monitors carbon deposition by measuring H2 formed during CH4 decomposition and affords information on the different catalytic species, deactivation process, reaction kinetics and carbon yields. The obtained results showed for FeMgO catalyst a simple TPCVD peak related to the production of carbon beginning at 760 degrees C with maximum at 800 degrees C followed by a rapid deactivation resulting in a low carbon yield. The addition of Mo to Fe/MgO catalyst completely changes the TPCVD profile with the formation of a new catalytic species active at temperatures higher than 900 degrees C, which is stable and continuously decomposes CH4 to produce high carbon yields. Raman, TG/DTG, Mössbauer, SEM, TEM, XRD and TPR analyses suggested that this active catalytic phase is likely related to Fe-Mo and Fe-Mo-C phases active to produce single wall and mainly multiwall carbon nanotubes.