Strong Immunity to Drain-Induced Barrier Lowering in ALD-Grown Preferentially Oriented Indium Gallium Oxide Transistors.

ABSTRACT

Drain-induced barrier lowering (DIBL) is one of the most critical obstacles degrading the reliability of integrated circuits based on miniaturized transistors. Here, the effect of a crystallographic structure change in InGaO [indium gallium oxide (IGO)] thin-films on the DIBL was investigated. Preferentially oriented IGO (po-IGO) thin-film transistors (TFTs) have outstanding device performances with a field-effect mobility of 81.9 ± 1.3 cm2/(V s), a threshold voltage (VTH) of 0.07 ± 0.03 V, a subthreshold swing of 127 ± 2.0 mV/dec, and a current modulation ratio of (2.9 ± 0.2) × 1011. They also exhibit highly reliable electrical characteristics with a negligible VTH shift of +0.09 (-0.14) V under +2 (-2) MV/cm and 60 °C for 3600 s. More importantly, they reveal strong immunity to the DIBL of 17.5 ± 1.2 mV/V, while random polycrystalline In2O3 (rp-In2O3) and IGO (rp-IGO) TFTs show DIBL values of 197 ± 5.3 and 46.4 ± 1.2 mV/V, respectively. This is quite interesting because the rp- and po-IGO thin-films have the same cation composition ratio (In/Ga = 82). Given that the lateral diffusion of oxygen vacancies from the source/drain junction to the channel region via grain boundaries can reduce the effective length (Leff) of the oxide channel, this improved immunity could be attributed to suppressed lateral diffusion by preferential growth. In practice, the po-IGO TFTs have a longer Leff than the rp-In2O3 and -IGO TFTs even with the same patterned length. The effect of the crystallographic-structure-dependent Leff variation on the DIBL was corroborated by technological computer-aided design simulation. This work suggests that the atomic-layer-deposited po-IGO thin-film can be a promising candidate for next-generation electronic devices composed of the miniaturized oxide transistors.