Engineering Co3O4@3DOM LaCoO3 multistage-pore nanoreactor with superior SO2 resistance for toluene catalytic combustion.

ABSTRACT

Sulfur dioxide poisoning is a significant factor in catalyst deactivation during the catalytic combustion of volatile organic compounds. In this study, we prepared the LaCoO3 and Co3O4 composite catalysts using both the Ship-in-Bottle and Building-Bottle-Around-Ship approaches. Three-dimensionally ordered macropores (3DOM LaCoO3) were utilized as nanoreactors to protect the active sites during the catalytic combustion of toluene, preventing SO2 poisoning. Additionally, we grew ZIF-67 confined in the nanoreactor to create a multistage-pore structure. The Co3O4@3DOM LaCoO3 catalysts exhibited excellent activity in the complete catalytic oxidation of toluene. Various characterization studies confirmed the presence of a significant number of Co3+ species and an abundance of surface weak acid sites in the Co3O4@3DOM LaCoO3 catalysts, which synergistically enhanced the conversion of VOCs at low temperatures. Notably, the multistage pore structure provided a favorable reaction environment, accelerating the adsorption and diffusion of toluene and intermediates, resulting in excellent sulfur resistance of the catalysts. Moreover, XPS analysis confirmed a strong interaction between Co3O4 and LaCoO3, promoting rapid electron transfer and increasing the activation of O2-. In situ DRIFTS experiments verified that toluene mainly follows the MvK mechanism over Co3O4@3DOM LaCoO3 catalysts, indicating the following reaction pathway toluene adsorption → benzyl alcohol → benzaldehyde → benzoate → anhydride → CO2 and H2O.