RESUMO
Uma superfície de cada um de quatro blocos foi polida e submetida aos seguintes tratamentos de superfície bloco A (HF+S) - microjateamento com Al2O3 de 50 μm (15 s), condicionamento com ácido HF a 9,5% (20 s) e aplicação de silano (3 min); bloco B (HF) - microjateamento e condicionamento com ácido HF; bloco C (S) - microjateamento e silano; e bloco D (CJ) - microjateamento com CoJet Sand e aplicação de silano. O adesivo Scotchbond Multi-Purpose Plus foi aplicado sobre a superfície dos blocos A, B e C, e o adesivo Visio-Bond do sistema CoJet, no D, todos polimerizados, e resina composta (Filtek Z250) foi adicionada em quatro incrementos de 1 mm e fotopolimerizada. Os blocos de resina-cerâmica foram, então, seccionados em dois eixos perpendiculares, produzindo cada um aproximadamente 40 corpos de prova, divididos em dois grupos grupo Imediato, dividido em quatro subgrupos HF+S/I (n = 19), HF/I (n = 19), S/I (n = 20) e CJ/I (n = 16), armazenados por 24 h em água destilada; e grupo 12m+Tc, dividido em quatro subgrupos HF+S/12m (n = 20), HF/12m (n = 20), S/12m (n = 20) e CJ/12m (n = 17), armazenados por 12 meses em saliva artificial, seguidos por termociclagem (800 ciclos). Os valores médios obtidos (HF+S/I = 56,85±16,52(a), HF/I = 51,69±11,34(ab), S/I = 50,73±12,37(ab), CJ/I = 40,13±9,27(bc), HF+S/12m = 42,29±17,34(b), HF/12m = 21,03±7,02(d), S/12m = 13,72±6,24(d), CJ/12m = 26,77±21,07(cd)) foram analisados estatisticamente (ANOVA 2). Observou-se interação entre tratamento de superfície e condição de armazenamento. Condicionamento da superfície cerâmica com ácido HF combinado com silanização propiciou maior μ-TBS à resina após 12 meses de armazenamento em saliva artificial e termociclagem...
ABSTRACT
One surface of each out of four blocks was polished and subjected to the following surface treatments A (HF + S) sandblasting with AL2O3 50 μm (15 s), etching with 9.5% HF (20 s) and silane application (3 min); B(HF) - sandblasting and etching with HF; C (S) sandblasting and silane; D (CJ) sandblasting with CoJet Sand and silane application. A three-step total-etch adhesive was applied (ScotchBond Multi-Purpose Plus) on the surface of the blocks A, B, and C, and the light-cured bonding material, proprietary of the CoJet system (Visio-Bond) on block D, light-cured, and composite resin (Filtek Z250) was added in four 1 mm increments and light cured. The ceramic-resin blocks were then sectioned into two perpendicular axes, each producing approximately 40 specimens, divided into two groups immediate group divided into four subgroups HF + s / i (n = 19) , HF / i (n = 19), S / I (n = 20) and cj / i (n = 16), stored for 24 h in distilled water; and group 12m + tc, divided into four subgroups s/12m + HF (n = 20) HF/12m (n = 20) s/12m (n = 20) and CJ/12m (n = 17) stored for 12 months in artificial saliva followed by thermocycling (800 cycles). The obtained average values (HF + s / i = 56.85 ± 16.52 (a) HF / i = 51.69 ± 11.34 (ab) s / i = 50.73 ± 12.37 (ab), CJ/ i = 40.13 ± 9.27 (bc) + HF s/12m = 42.29 ± 17.34 (b), HF/12m = 21.03 ± 7.02 (d), s / 12m = 13.72 ± 6.24 (d), 26.77 ± 21.07 CJ/12m = (cd)) were statistically analyzed (2-way ANOVA). Interaction between surface treatment and storage conditions were observed. Conditioning of the ceramic surface with HF associated with silanization provided greater μ-TBS values to resin after 12 months of storage in artificial saliva and thermocycling...
Key words
Search on Google
Collection:
01-internacional
Database:
LILACS
Main subject:
Resins, Synthetic
/
Silanes
/
Ceramics
/
Dental Restoration, Permanent
Limits:
Humans
Language:
Pt
Journal:
Clín. int. j. braz. dent
Journal subject:
ODONTOLOGIA
Year:
2014
Document type:
Article
Affiliation country:
Brazil