Condensation of Si-rich region inside soda-lime glass by parallel femtosecond laser irradiation.

ABSTRACT

Local melting and modulation of elemental distributions can be induced inside a glass by focusing femtosecond (fs) laser pulses at high repetition rate (>100 kHz). Using only a single beam of fs laser pulses, the shape of the molten region is ellipsoidal, so the induced elemental distributions are often circular and elongate in the laser propagation direction. In this study, we show that the elongation of the fs laser-induced elemental distributions inside a soda-lime glass could be suppressed by parallel fsing of 250 kHz and 1 kHz fs laser pulses. The thickness of a Si-rich region became about twice thinner than that of a single 250 kHz laser irradiation. Interestingly, the position of the Si-rich region depended on the relative positions between 1 kHz and 250 kHz photoexcited regions. The observation of glass melt during laser exposure showed that the vortex flow of glass melt occurred and it induced the formation of a Si-rich region. Based on the simulation of the transient temperature and viscosity distributions during laser exposure, we temporally interpreted the origin of the vortex flow of glass melt and the mechanism of the formation of the Si-rich region.