Surface Treatments on Repair Bond Strength of Aged Resin Composites.

ABSTRACT

Aims: The aim was to evaluate the effect of different surface treatments on the repair shear bond strength of aged resin composites. Materials and Methods: Forty cylindrical-shaped specimens were treated from each material: Tetric Evo Ceram, Neo Spectra, and Filtek Ultimate Universal Restorative and allocated into four groups according to the surface treatment planned to use Group 1 diamond, Group 2 silica coating, Group 3 carbide burs, and Group 4 control group. Following the surface treatment, composites were repaired with flowable resins. The shear bond strength was tested using a universal testing machine at a crosshead speed of 0.5 mm/min. The fracture mode was assessed under 50× magnification. The data were analyzed statistically using a two-way analysis of variance (ANOVA) test followed by a one-way ANOVA test. Multiple comparison procedures were performed using Tukey's test. The level of significance was set at P < 0.05. Results: The lowest mean value of the shear bond strength was for the Filtek Ultimate Universal Restorative in the control group, whereas the highest mean value was in the silica group. Silica and carbide groups had significantly higher mean values of the shear bond strength than diamond and control groups in Tetric EvoCeram and Filtek Ultimate Universal Restorative. In contrast, in Neo Spectra St HV, the carbide group had a higher mean value but was not statistically significant. Conclusion: Combinations of mechanical and chemical retentive systems enhance the shear bond strength of the repair composite to the aged composite. Among the different surface treatments employed in this study, silica and carbide groups show higher repair bond strength of new composite to aged composite.