Experimental toothpastes containing ß-TCP nanoparticles functionalized with fluoride and tin to prevent Erosive Tooth Wear.

ABSTRACT

OBJECTIVES: The present study aimed to synthesize toothpastes containing Beta- TriCalcium Phosphate (ß-TCP) nanoparticles, functionalized with fluoride and tin, and test their ability to reduce erosive tooth wear (ETW). METHODS: Toothpastes were synthesized with the following active ingredients 1100 ppm of fluoride (as sodium fluoride, F-), 3500 ppm of tin (as stannous chloride, Sn2+), and 800 ppm of ß-TCP (Sizes a - 20 nm; and b - 100 nm). Enamel specimens were randomly assigned into the following groups (n = 10) 1. Commercial toothpaste; 2. Placebo; 3 F-; 4. F- + ß-TCPa; 5. F- + ß-TCPb; 6. F- + Sn2+; 7. F- + Sn2+ + ß-TCPa and 8. F- + Sn2+ + ß-TCPb. Specimens were subjected to erosion-abrasion cycling. Surface loss (in µm) was measured by optical profilometry. Toothpastes pH and available F- were also assessed. RESULTS: Brushing with placebo toothpaste resulted in higher surface loss than brushing with F- (p = 0.005) and F- + ß-TCPb (p = 0.007); however, there was no difference between F- and F- + ß-TCPb (p = 1.00). Commercial toothpaste showed no difference from Placebo (p = 0.279). The groups F-, F- + ß-TCPa, F- + ß-TCPb, F- + Sn2+, F- + Sn2+ + ß-TCPa and F- + Sn2+ + ß-TCPb were not different from the commercial toothpaste (p > 0.05). Overall, the addition of ß-TCP reduced the amount of available fluoride in the experimental toothpastes. The pH of toothpastes ranged from 4.97 to 6.49. CONCLUSIONS: Although toothpaste containing ß-TCP nanoparticles protected enamel against dental erosion-abrasion, this effect was not superior to the standard fluoride toothpaste (commercial). In addition, the functionalization of ß-TCP nanoparticles with fluoride and tin did not enhance their protective effect. CLINICAL SIGNIFICANCE: Although ß-TCP nanoparticles have some potential to control Erosive Tooth Wear, their incorporation into an experimental toothpaste appears to have a protective effect that is similar to a commercial fluoride toothpaste.