Do irrigation solutions influence the bond interface between glass fiber posts and dentin?

ABSTRACT

Abstract The aim of this study was to evaluate the push-out bond strength and interface permeability of glass-fiber posts in different regions of post space (cervical, middle, and apical) submitted to different irrigation solutions. Ninety single-rooted human teeth were submitted to endodontic treatment and divided into five groups, according to irrigation solutions distilled water, 5.25% NaOCl, 25% polyacrylic acid, 2% chlorhexidine, and 23 ppm Ag NP dispersion. Each group was divided in 3 subgroups (n=6) according to cementation SBU Adper Scotchbond Universal + RelyX ARC; U200 RelyX U200; MCE MaxCem Elite. Bond strength and sealing ability were measured in different areas of post space. The data was subjected to ANOVA and Fisher's test (a=0,05). The silver nanoparticle solution showed highest bond strength values and lowest interface permeability in all thirds analyzed for SBU group. In the U200 group, the highest bond strength values were found for sodium hypochlorite solution, with significant difference between this solution and polyacrylic acid. A decrease in bond strength values in cervical to apical direction was found for MCE group and the same behavior were found for others groups. Regarding interface permeability, use of silver nanoparticle solution resulted in lower values in cervical and apical thirds. There was a decrease in bond strength in cervical to apical direction. Different irrigation solutions and intraradicular depth influenced the bond strength and interface permeability of adhesive material to dentin substrate. Silver nanoparticle solution can effectively be used as an irrigation agent in post space prior to fiber post cementation process.

RESUMO

Resumo O objetivo deste trabalho foi avaliar a resistência de união e permeabilidade da interface de pinos de fibra de vidro nos diferentes terços da dentina intrarradicular (cervical, médio e apical) submetidos a diferentes agentes irrigantes. Noventa dentes unirradiculares humanos foram submetidos ao tratamento endodôntico e foram divididos em cinco grupos de acordo com os agentes irrigantes água destilada, hipoclorito de sódio 5,25%, ácido poliacrílico 25%, clorexidina 2% e dispersão de nanopartícula de prata à 23 ppm. Os grupos foram divididos em 3 subgrupos (n=6) de acordo com a técnica adotada para cimentação adesiva dos pinos de fibra de vidro Grupo SBU sistema adesivo ScotchbondTM Universal + cimento resinoso RelyX ARC; Grupo U200 cimento resinoso autoadesivo RelyX U200; Grupo MCE cimento resinoso autoadesivo Maxcem Elite. A resistência de união e a permeabilidade da interface foram mensurados em diferentes áreas da dentina intrarradicular. Os dados foram submetidos a ANOVA e teste de Fisher (a=0,05). Amostras representativas foram levadas à microscopia eletrônica de varredura. A solução de nanopartícula de prata apresentou os maiores valores de resistência de união em todos os terços analisados para o grupo SBU. No grupo U200, os maiores valores foram encontrados para a solução de hipoclorito de sódio, com diferença para o ácido poliacrílico. Observou-se uma diminuição nos valores de resistência de união na direção cérvico-apical para o grupo MCE e o mesmo comportamento foram encontrados para os demais grupos. Com relação a permeabilidade da interface, o uso da solução de nanopartícula de prata resultou em menores valores nos terços cervical e apical. Houve diminuição dos valores de resistência de união no sentido cérvico-apical. As diferentes soluções irrigantes, bem como a profundidade intrarradicular influenciaram a resistência de união e permeabilidade da interface dos materiais adesivos ao substrato dentinário. A nanopartícula de prata pode ser utilizada como agente irrigador do conduto radicular previamente à cimentação de pinos de fibra de vidro.