Avaliação de propriedades físico-químicas, tempo de endurecimento e drenagem de um cimento endodôntico adicionado ao MTA em diferentes proporções / Evaluation of physico-chemical properties, time of hardening and draining of an endodontic sealer added to mta in different proportions
Rev. bras. odontol
; 76(1): 1-5, jan. 2019. tab
Article
en En
| LILACS
| ID: biblio-1120365
Biblioteca responsable:
BR485.1
RESUMO
Objetivo:
o objetivo desta pesquisa foi avaliar o tempo e o fluxo de endurecimento do cimento AH-PLUS e MTA nas proporções de 10%, 20% e 30%, a fim de adicionar a capacidade de estimular a deposição de tecido duro. Material eMétodos:
Para o teste de fluxo, 0,5 ml de cimento foram depositados em uma placa de vidro e outra placa foi adicionada com uma carga adicional, após 10 minutos a carga foi removida e o diâmetro do círculo formado pelo cimento foi medido com um Bússola digital. Para o tempo de endurecimento, foram utilizados moldes cilíndricos preenchidos com o cimento testado, mantidos dentro de um forno e os testes de agulha de Gillmore foram realizados no material em intervalos de 60 segundos até que as marcas não fossem visíveis na superfície do cimento testado.Resultados:
Na vazão, os valores obtidos foram 41,1 mm (10% MTA), 32,86 mm (20% MTA), 21,91 mm (30% MTA), 24,41 mm AHPlus® e 26,47 mm MTA Fillapex®. O tempo de endurecimento encontrado nesta pesquisa foi de 1631 'em proporção (10% MTA), 628,4 em proporção (20% MTA), 567' em proporção (30% MTA), 767 em AH Plus e Fillapex MTA não. presou dentro de 6 semanas.Conclusão:
concluiu-se que a adição de 10%, 20% e 30% de MTA ao AH Plus não alterou as propriedades do fluxo e o tempo estabelecidoABSTRACT
Objective:
evaluate the hardening time and flow of AH-PLUS and MTA cement in the proportions of 10%, 20% and 30% in order to add the ability to stimulate the deposition of hard tissue. Material andMethods:
For the flow test, 0.5 ml of cement was deposited on a glass plate and another plate was added with an additional charge, after 10 minutes the charge was removed and the diameter of the circle formed by the cement was measured with a digital compass. For the hardening time, cylindrical molds filled with the tested cement were used, kept inside a kiln and Gillmore needle tests were performed on the material at 60 second intervals until the marks were not visible on the surface of the tested cement.Results:
In the flow rate, the values obtained were 41.1mm (10% MTA), 32.86mm (20% MTA), 21.91mm (30% MTA), 24.41mm AHPlus® and 26.47mm MTA Fillapex®. The hardening time found in this survey was 1631 'in proportion (10% MTA), 628.4 in proportion (20% MTA), 567' in proportion (30% MTA), 767 in AH Plus and Fillapex MTA did not. took prey within 6 weeks.Conclusion:
it was concluded that the addition of 10%, 20% and 30% of MTA to AH Plus did not change the flow properties and the established timePalabras clave
Texto completo:
1
Colección:
01-internacional
Base de datos:
LILACS
Asunto principal:
Cementos Dentales
/
Materiales Dentales
/
Endodoncia
Idioma:
En
Revista:
Rev. bras. odontol
Asunto de la revista:
ODONTOLOGIA
Año:
2019
Tipo del documento:
Article
País de afiliación:
Brasil