In vitro evaluation of the antimicrobial activity of endodontic sealers

ABSTRACT

The purpose of this study is to evaluate the antimicrobial activity of the endodontic sealers N-Rickert, Sealapex, AH Plus, Mineral Trioxide Aggregate (MTA) and portland cement. The Agar diffusion method was used in plates previously inoculated with the following microorganisms C. albicans, S. aureus, E. faecalis, E. coli. The diameters of microbial inhibition zones were measured after 24 hours of incubation in kiln at 37°C. According to the methodology used, it was possible to conclude that only the sealers AH Plus and N-Rickert presented antimicrobial activity against C. albicans, S. aureus, and E. coli; no antimicrobial activity in MTA, Sealapex and portland cement was observed. N-Rickert presented the largest inhibition zones varying from 8 to 18 mm, and the microorganism E. faecalis was resistant against all sealers tested.

RESUMO

O objetivo deste estudo é avaliar a capacidade antimicrobiana dos cimentos obturadores de canal N-Rickert, Sealapex, AH Plus e também do Agregado Trióxido Mineral (MTA) e Cimento de Portland. O método utilizado foi a difusão em Agar, em placas previamente inoculadas com os seguintes microorganismos C. albicans, S. aureus, E. faecalis, E. coli. A leitura do diâmetro do halo de inibição do crescimento microbiano foi realizada, após 24 horas de incubação, em estufa a 37°C. De acordo com a metodologia empregada, foi possível concluir que somente os cimentos obturadores AH Plus e N-Rickert apresentaram atividade antimicrobiana contra C. albicans, S. aureus e E. coli; não foi observada atividade antimicrobiana no cimento de Portland, MTA e Sealapex. O cimento N-Rickert apresentou halos de inibição maiores variando de 8 a 18 mm. O microorganismo E. faecalis foi resistente contra todos os cimentos testados.