A castor oil-containing dental luting agent: effects of cyclic loading and storage time on flexural strength
J. appl. oral sci
; 22(6): 496-501, Nov-Dec/2014. tab, graf
Artículo
en Inglés
| LILACS, BBO - Odontología
| ID: lil-732584
Biblioteca responsable:
BR1.1
ABSTRACT
Favorable results in the use of castor oil polyurethane (COP) as pulp capping, membrane material, sealer, mouthwash and in bone repair, associated with the fact that Ricinus communis is not derived from petroleum and it is abundant in Brazil, encourage researches in the development of luting agents. Objectives This study compared the flexural strength (FS) of a castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate (COP10) with RelyX ARC (RX) after mechanical cycling (MC) and distilled water storage. Material and Methods Sixty-four specimens (25x2x2 mm) were fabricated and divided into two groups, COP10 and RX (control). Each group was divided into 4 subgroups (n=8) according to the storage time, 24 hours (24 h) or 60 days (60 d), and the performance (MC+FS) or not (only FS) of the mechanical cycling test. The FS (10 kN; 0.5 mm/min) and MC tests (10,000 cycles, 5 Hz, 0.5 mm/min) were carried out using an MTS-810 machine. The data were analyzed using ANOVA (α=0.05). Results The obtained FS (MPa) values were COP10 24h- 19.04±2.41; COP10 60d- 17.92±3.54; RX 24h- 75.19±3.43; RX 60d- 88.77±6.89. All the RX specimens submitted to MC fractured, while the values for COP10 after MC were as follows COP10 24h- 17.90±1.87 and COP10 60d- 18.60±1.60. Conclusions A castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate is resistant to mechanical cycling without decreases in flexural strength. However, mean COP10 showed only about 25% of the RelyX ARC mean flexural strength. .
Texto completo:
Disponible
Colección:
Bases de datos internacionales
Base de datos:
BBO - Odontología
/
LILACS
Asunto principal:
Polietilenglicoles
/
Ácidos Polimetacrílicos
/
Poliuretanos
/
Carbonato de Calcio
/
Aceite de Ricino
/
Bisfenol A Glicidil Metacrilato
/
Cementos Dentales
Idioma:
Inglés
Revista:
J. appl. oral sci
Asunto de la revista:
Odontología
Año:
2014
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
University of São Paulo/BR