Efeito do trimetafosfato de sódio e do fluoreto sobre a solubilidade da hidroxiapatita: estudo in vitro / Effect of sodium trimetaphosphate and fluoride on hydroxyapatite solubility: an in vitro study
Araçatuba; s.n; 2014. 59 p. tab, ilus, graf.
Thesis en En | LILACS | ID: lil-761293
Biblioteca responsable: BR186.1
RESUMO
O objetivo deste estudo foi avaliar o efeito de diferentes concentrações de trimetafosfato de sódio (TMP) associado ao fluoreto (F) sobre a solubilidade da hidroxiapatita (HA), bem como as propriedades físicas e químicas da HA depois de um ciclo de pH. O de HA sintética (1,0 g; n= 6) foi misturado com soluções de TMP nas concentrações de 0; 0,1; 0,2; 0,4; 0,6; 0,8; 1,0; 2,0; 4,0; 6,0; 8,0 e 10%, associadas ao F nas concentrações de 0, 100, 250 e 500 ppm F, durante 2 min. A suspensão foi filtrada e o precitado foi seco por 24 horas a 37°C e moído. Depois do tratamento, as amostras de HA tratada foram submetidas a um ciclo de pH. As amostras de HA ciclada foram caracterizadas por energia dispersiva de raios-X (EDX), espectroscopia de infravermelho (FTIR) e difração de raios-X (DRX). Depois, as concentrações de F solúvel em base e em ácido, cálcio (Ca) e fósforo (P) foram determinadas na HA ciclada, assim como as concentrações de P e F no sobrenadante. Os dados de F, Ca, P e proporção molar Ca/P na HA, e F e P no sobrenadante foram submetidas à Análise de Variância e teste de Student-Newman-Keuls (p<0,05). Houve uma redução do tamanho dos cristais de HA com o aumento da concentração de TMP. A HA tratada com 500 ppm F e TMP a 1% produziu uma HA com cristalitos de tamanho maiores. O FTIR mostrou uma redução na intensidade das bandas de fosfatos e carbonato quando comparado à HA sintetizada. As maiores proporções Ca/P foram observadas na HA tratada com TMP entre 0,4% e 1% quando combinado com 250 ppm F, e entre 0,4% e 2% em associação com 500 ppm F (p<0,05). Um aumento na concentração de TMP levou a uma redução na incorporação de F solúvel em ácido na estrutura do cristal para todos os grupos, nas duas situações (depois do tratamento e depois do ciclo de pH) (p<0,05). Adicionalmente, um aumento na concentração de TMP também proporcionou uma maior adsorção de TMP à HA para as soluções de 0 e 100 ppm F, mas menor para as soluções de 250 e 500 ppm F (p<0,05)...
ABSTRACT
The aim of this study was to evaluate the effect of different concentrations of sodium trimetaphosphate (TMP) associated with fluoride (F) on hydroxyapatite (HA) solubility, as well as in chemical and physical properties of HA after a pH-cycle. Synthetic HA powder (1.0 g; n= 6) was mixed with solutions of TMP at 0, 0.1, 0.2, 0.4, 0.6, 0.8, 1.0, 2.0, 4.0, 6.0, 8.0 and 10%, associated with fluoride at 0, 100, 250 and 500 ppm F, during 2 min. The suspension was filtered and the precipitates were dried for 24 h at 37°C and grinded. After the treatment, HA samples were submitted to a pH-cycle. Post-cycled HA samples were analyzed by energy-dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and X-ray diffraction (XRD). Afterwards, the concentration of alkali and acid soluble F, Ca and P were determined in post-cycled HA, as well as P and F in the supernatant. The data of F, Ca, P, Ca/P ratio of HA, and F and P in the supernatant were submitted to ANOVA and Student-Newman-Keuls’ test (p<0.05). A reduction of the size of the HA crystallites was seen with increasing TMP concentrations in the solutions. HA treated with 500 ppm F and 1% TMP produced an HA with crystallites of larger size. The FTIR showed a reduction in the bands corresponding to phosphates and to carbonate for all groups when compared to the HA synthetized. The highest Ca/P ratios were observed for HA treated with TMP concentrations between 0.4% and 0.8% when combined with 250 ppm F, and between 0.4% and 2% in association with 500 ppm F (p<0.05). The increase of TMP led a reduced acid-soluble F incorporation in HA for all groups, both immediately after treatment and after the pH cycle (p<0.05). Additionally, the increase in TMP concentrations led to higher P adsorption to HA for the 0 and 100 ppm F solutions, but lower for the 250 and 500 ppm F solutions (p<0,05). The results indicate that the mechanism of action of TMP seems to be related with the TMP adsorption to crystal structural...
Asunto(s)
Palabras clave
Texto completo: 1 Colección: 01-internacional Base de datos: LILACS Asunto principal: Polifosfatos / Durapatita / Fluoruros Límite: Humans Idioma: En Año: 2014 Tipo del documento: Thesis Pais de publicación: Brasil
Texto completo: 1 Colección: 01-internacional Base de datos: LILACS Asunto principal: Polifosfatos / Durapatita / Fluoruros Límite: Humans Idioma: En Año: 2014 Tipo del documento: Thesis Pais de publicación: Brasil