Dielectric relaxations in ultrathin isotactic PMMA films and PS-PMMA-PS trilayer films.
Eur Phys J E Soft Matter
; 12 Suppl 1: S109-12, 2003 Nov.
Article
en En
| MEDLINE
| ID: mdl-15011027
ABSTRACT
The local and cooperative dynamics of supported ultrathin films ( L = 6.4 - 120 nm) of isotactic poly(methyl methacrylate) (i-PMMA, Mn = 118 x 10(3) g/mol) was studied using dielectric relaxation spectroscopy for a wide range of frequencies (0.1 Hz to 10(6) Hz) and temperatures (250 - 423 K). To assess the influence of the PMMA film surfaces on the glass transition dynamics, two different sample geometries were employed a single layer PMMA film with the film surfaces in direct contact with aluminum films which act as attractive, hard boundaries; and a stacked polystyrene-PMMA-polystyrene trilayer film which contains diffuse PMMA-PS interfaces. For single layer films of i-PMMA, a decrease of the glass transition temperature T(g) by up to 10 K was observed for a film thickness L < 25 nm (comparable to R(EE)), indicated by a decrease of the peak temperature T(alpha) in the loss epsilon(")(T) at low and high frequencies and by a decrease in the temperature corresponding to the maximum in the apparent activation energy E(a)(T) of the alpha-process. In contrast, measurements of i-PMMA sandwiched between PS-layers revealed a slight (up to 5 K) increase in T(g) for PMMA film thickness values less than 30 nm. The slowing down of the glass transition dynamics for the thinnest PMMA films is consistent with an increased contribution from the less mobile PMMA-PS interdiffusion regions.
Buscar en Google
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
En
Revista:
Eur Phys J E Soft Matter
Asunto de la revista:
BIOFISICA
Año:
2003
Tipo del documento:
Article
País de afiliación:
Países Bajos