Structural Properties of Al-O Monolayers in SiO2 on Silicon and the Maximization of Their Negative Fixed Charge Density.
ACS Appl Mater Interfaces
; 10(36): 30495-30505, 2018 Sep 12.
Article
en En
| MEDLINE
| ID: mdl-30110151
ABSTRACT
Al2O3 on Si is known to form an ultrathin interfacial SiO2 during deposition and subsequent annealing, which creates a negative fixed charge ( Qfix) that enables field-effect passivation and low surface recombination velocities in Si solar cells. Various concepts were suggested to explain the origin of this negative Qfix. In this study, we investigate Al-O monolayers (MLs) from atomic layer deposition (ALD) sandwiched between deliberately grown/deposited SiO2 films. We show that the Al atoms have an ultralow diffusion coefficient (â¼4 × 10-18 cm2/s at 1000 °C), are deposited at a constant rate of â¼5 × 1014 Al atoms/(cm2 cycle) from the first ALD cycle, and are tetrahedral O-coordinated because the adjacent SiO2 imprints its tetrahedral near-order and bond length into the Al-O MLs. By variation in the tunnel-SiO2 thickness and the number of Al-O MLs, we demonstrate that the tetrahedral coordination alone is not sufficient for the formation of Qfix but that a SiO2/Al2O3 interface within a tunneling distance from the substrate must be present. The Al-induced acceptor states at these interfaces have energy levels slightly below the Si valence band edge and require charging by electrons from either the Si substrate or from Si/SiO2 dangling bonds to create a negative Qfix. Hence, tunneling imposes limitations for the SiO2 and Al2O3 layer thicknesses. In addition, Coulomb repulsion between the charged acceptor states results in an optimum number of Al-O MLs, i.e., separation of both interfaces. We achieve maximum negative Qfix of â¼5 × 1012 cm-2 (comparable to thick ALD-Al2O3 on Si) with â¼1.7 nm tunnel-SiO2 and just seven ALD-Al2O3 cycles (â¼8 Å) after optimized annealing at 850 °C for 30 s. The findings are discussed in the context of a passivating, hole-selective tunnel contact for high-efficiency Si solar cells.
Texto completo:
1
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
En
Revista:
ACS Appl Mater Interfaces
Asunto de la revista:
BIOTECNOLOGIA
/
ENGENHARIA BIOMEDICA
Año:
2018
Tipo del documento:
Article
País de afiliación:
Australia