Enhanced Thermoelectric Performance of Bi0.46Sb1.54Te3 Nanostructured with CdTe.
ACS Appl Mater Interfaces
; 12(23): 26330-26341, 2020 Jun 10.
Article
en En
| MEDLINE
| ID: mdl-32401006
ABSTRACT
Cd-containing polycrystalline Bi0.46Sb1.54Te3 samples with precisely controlled phase composition were synthesized by conventional melting-quenching-annealing technique and a melt-spinning method. The pseudo ternary phase diagram for Cd-Bi/Sb-Te in the region near Bi0.46Sb1.54Te3 was systematically studied. Cd serves as an acceptor dopant contributing holes, whereas for samples doped with CdTe, the combined effects of the substitution of Sb/Bi with Cd and the formation of Sb/BiTe antisite defects leads to the increase in hole concentration. Moreover, upon doping with Cd, the lattice thermal conductivity decreases significantly owing to the intensified point defect phonon scattering. The sample with Cd content of 0.01 attains the maximum ZT of 1.15 at 425 K. The utilization of melt-spinning method brings about the in situ nanostructured CdTe and grain size refinement, which further reduce the lattice thermal conductivity while preserving excellent electrical performance. As a result, a higher ZT of 1.30 at 425 K is realized with CdTe content x = 0.005.
Texto completo:
1
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
En
Revista:
ACS Appl Mater Interfaces
Asunto de la revista:
BIOTECNOLOGIA
/
ENGENHARIA BIOMEDICA
Año:
2020
Tipo del documento:
Article
País de afiliación:
China