In Vitro Performance of Different Universal Adhesive Systems on Several CAD/CAM Restorative Materials After Thermal Aging.

ABSTRACT

OBJECTIVE: To evaluate the microshear bond strength (mSBS) of 10 universal adhesive systems applied on five different CAD/CAM restorative materials, immediately and after thermal aging. METHODS AND MATERIALS Five CAD/CAM materials were selected 1) feldspathic glass ceramic (FeCe); 2) pre-polymerized reinforced resin composite (ReRC); 3) leucite-reinforced glass ceramic (LeGC); 4) lithium disilicate (LiDi); and 5) yttrium-stabilized zirconium dioxide (ZiDi). For each material, 15 blocks were cut into four rectangular sections (6 × 6 × 6 mm; n=60 per group) and processed as recommended by the respective manufacturer. For each indirect material, the following adhesive systems were applied according to the respective manufacturer's instructions 1) AdheSE Universal [ADU]; 2) All-Bond Universal [ABU]; 3) Ambar Universal [AMB]; 4) Clearfil Universal Bond [CFU]; 5) Futurabond U [FBU]; 6) One Coat 7 Universal [OCU]; 7) Peak Universal Bond [PUB]; 8) Prime&Bond Elect [PBE]; 9) Scotchbond Universal Adhesive [SBU]; 10) Xeno Select [XEN, negative control]. After the application of the adhesive system, cylinder-shaped transparent matrices were filled with a dual-curing resin cement (NX3) and light cured. Specimens were tested in shear mode at 1.0 mm/min (mSBS), after 24 hours and 10,000 thermal cycles (TC). All data were submitted to statistical analysis (α=0.05). RESULTS: For FeCe, there was no significant decrease in mean mSBS for AMB, FBU, and SBU after TC when compared at 24 hours. For ReRC, AMB and SBU showed higher mean mSBS when compared to CFU and XEN, after 24 hours and TC. For LiDi, FBU and OCU showed higher mean mSBS when compared to CFU and XEN, after 24 hours and TC. For LeGC, AMB and PUB showed higher mean mSBS when compared to XEN, after 24 hours and TC. For ZiDi, OCU and SBU showed higher mean mSBS when compared to XEN, after 24 hours and TC. In addition, PBE and XEN showed the lowest mean mSBS after TC with higher percentage of bond strength reduction. CONCLUSIONS: The mean mSBS among the different universal adhesives varied widely for each CAD/CAM material used. In addition, most universal adhesives underwent a statistically significant bond strength reduction after TC.