Fast and High-Yield Anhydrous Synthesis of Ti3 C2 Tx MXene with High Electrical Conductivity and Exceptional Mechanical Strength.

ABSTRACT

2D transition metal carbides or nitrides (MXenes) have attracted considerable attention from materials scientists and engineers owing to their physicochemical properties. Currently, MXenes are synthesized from MAX-phase precursors using aqueous HF. Here, in order to enhance the production of MXenes, an anhydrous etching solution is proposed, consisting of dimethylsulfoxide as solvent with its high boiling point, NH4 HF2 as an etchant, CH3 SO3 H as an acid, and NH4 PF6 as an intercalant. The reaction temperature can be increased up to 100 °C to accelerate the etching and delamination of Ti3 AlC2 MAX crystals; in addition, the destructive side reaction of the produced Ti3 C2 Tx MXene is suppressed in the etchant. Consequently, the etching reaction is completed in 4 h at 100 °C and produces high-quality monolayer Ti3 C2 Tx with an electrical conductivity of 8200 S cm-1 and yield of over 70%. The Ti3 C2 Tx MXene fabricated via this modified synthesis exhibits different surface structures and properties arising from more F-terminations than those of Ti3 C2 Tx synthesized in aqueous HF2 T. The atypical surface structure of Ti3 C2 Tx MXene results in an exceptionally high ultimate tensile strength (167 ± 8 MPa), which is five times larger than those of Ti3 C2 Tx MXenes synthesized in aqueous HF solution (31.7 ± 7.8 MPa).