A facile strategy to prepare FeNx decorated PtFe intermetallic with excellent acidic oxygen reduction reaction activity and stability.

ABSTRACT

The construction of low-Pt-content intermetallic on carbon supports has been verified as a promising method to promote the activity of the oxygen reduction reaction (ORR). In this study, we have developed a simple and effective strategy to obtain a well-designed CNT-PtFe-PPy precursor. This precursor contains modulated Pt- and Fe-based content dispersed in polypyrrole (PPy) chain segments, which are in-situ generated on the templates of carbon nanotubes (CNTs). Subsequent pyrolysis of the CNT-PtFe-PPy precursor produces a CNT-PtFe@FeNC catalyst, which contains both Fe-Nx and PtFe intermetallic active sites. Due to the highly efficient dispersion of active species, the CNT-PtFe@FeNC electrocatalyst displays a 9.5 times higher specific activity (SA) and 8.5 times higher mass activity (MA) than those of a commercial Pt/C catalyst in a 0.1 M HClO4 solution. Additionally, these results, combined with excellent durability (the SA and MA maintained 94 % and 91 % of initial activity after a 10-k cycle accelerated durability test), represent among the best performance achieved so far for Pt-based ORR electrocatalysts. Furthermore, density functional theory (DFT) calculations revealed that the presence of Fe-N4 species reduces the adsorption energy between the PtFe intermetallic compound and OH*, accelerating the ORR process.