Insights into the underpinning effect of graphene in Cu1Mn10 on enhancing the low-temperature catalytic activity for CO oxidation.

CO emission is a critical issue of industrial processes such as steel-smelting, cement manufacturing, and waste incineration. Catalytic oxidation based on Cu-Mn binary catalysts shows great potential for efficient removal of CO, whereas their practical applicability is limited by the inferior low-temperature catalytic activity and the high catalyst cost owing to a substantial quantity of Cu. In this study, doping graphene is designed to adjust the electron transfer capability to improve the low-temperature catalytic activity as well as reduce the amount of Cu, and thereby Cu1Mn10 catalysts doped with slight amounts of graphene (x%G-Cu1Mn10, x is 1∼5) were fabricated. It was found that the introduction of graphene could form effective electron transport channels to enhance the intermetallic interaction and oxygen vacancy generation, thus improving the low-temperature catalytic performance of the Cu1Mn10 catalyst. Among all the catalysts, 4%G-Cu1Mn10 exhibited the highest activity, achieving CO conversion of 92% at 110 °C at a weight hourly space velocity of 120,000 mL/(g∙h). The introduction of graphene also enabled the catalyst with excellent catalytic activity and stability at a relative humidity of 70%. Attractively, 4%G-Cu1Mn10 can be further loaded into the polyester fabric, presenting great application potentials in the effective elimination of CO during the dust removal process since the flue gas temperature in the dust collector is just around the T90% and the catalyst that is inside of fabric fiber rather than on the fabric surface can be rarely influenced by the dust. In general, doping graphene provides a facile method to enhance the low-temperature activities of the Cu-Mn binary catalysts and cut down the use of valuable Cu, showing great application potential.