Fracture resistance of CAD/CAM tooth-colored versus cast metal post-and-core restorations in root filled teeth: An in vitro study.

ABSTRACT

Purpose: This study investigated the fracture resistance and failure modes of custom-fabricated post- and core dental restorations using various CAD/CAM materials. Materials and Methods: Seventy-five mandibular second premolars were allocated to five groups (n = 15) and prepared for standardized post and core restorations. The groups included a control group comprising cast metal and four CAD/CAM materials Vita Enamic, Shofu HC, Trilor, and PEKK. Fracture resistance was assessed using a compressive force at a crosshead speed of 1 mm/min until failure occurred. Data were analyzed using one-way analysis of variance (ANOVA) and chi-square tests. Results: The metal group had the highest fracture resistance (244.41 ± 75.20 N), with a significant variance compared to that in the CAD/CAM groups (p < 0.001). No significant differences were observed among the non-metallic groups. Conclusions: While several CAD/CAM materials displayed satisfactory flexural properties, cast metal posts showed superior fracture resistance in endodontically treated teeth but were mostly associated with catastrophic failure. The clinical application of CAD/CAM materials for post-core restorations presents a viable alternative to traditional metal posts, potentially reducing the risk of unfavorable fractures.