Avaliação da microestrutura, microdureza e resistência à corrosão de juntas soldadas de uma liga de Ni-Cr obtidas através de diferentes processos de soldagem / Evaluation of the microstructure, hardness and corrosion resistance of welded joints of a Ni-Cr alloy obtained by different welding processes
Rio de Janeiro; s.n; 2013. 197 p. ilus, tab, graf.
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-867028
Biblioteca responsável: BR1366.1
Localização: BR1366.1; 616.314, M433, TO 721
RESUMO
Este trabalho avaliou o comportamento eletroquímico do metal de base (MB) de uma liga a base de níquel-cromo em relação a juntas soldadas desta liga obtidas pelos processos de brasagem (BRA) e Tungsten Inert Gas (TIG), imersos em saliva artificial com pH 2,5 e 5,5. Foram também realizados ensaios de microdureza e caracterização microestrutural, por meio de microscopia óptica e eletrônica de varredura e análise química semi-quantitativa por EDS, nos grupos MB, TIG, BRA e no cordão de solda a laser (LAS). O MB apresentou uma matriz rica em níquel e cromo, distribuída em um arranjo dendrítico típico, apresentando inclusões metálicas de silício e titânio, além de porosidades. As soldas TIG e LAS revelaram uma microestrutura mais refinada que o MB, mostrando, entretanto, uma mesma composição química e distribuição de seus elementos. A solda BRA apresentou diferenças marcantes em sua microestrutura, composição química e distribuição de seus elementos em relação ao MB. Os dados de microdureza Vickers (HV), potencial de corrosão (Ecorr) e densidade de corrente de corrosão (jcorr) foram analisados com ANOVA e teste de Tukey (p<0,05). Para determinação da influência do pH quanto a resistência à corrosão dos grupos MB, TIG e BRA, empregou-se o teste t de Student (p<0,05). O MB apresentou menor média de microdureza (256,13 ± 9,39 HV), seguido pelos grupos TIG (271,53 ± 8,07 HV), LAS (303,73 ± 13,93 HV) e BRA (551,99 ± 37,73 HV). Em pH 2,5 as médias do Ecorr (mV) para o MB, TIG e BRA foram, respectivamente, -67,9 ± 8,43, -52,78 ± 16,74, e -284,33 ± 19,04; e em pH 5,5, médias de -54,03 ± 21,15, -62,08 ± 20,16 e -278,8 ± 28,96. Os valores médios de jcorr (µA.cm-2) para o MB, TIG e BRA em pH 2,5 foram, respectivamente, 2,49 ± 0,95, 5,584 ± 1,64 e 27,45 ± 4,9; e em pH 5,5, médias de 1,929 ± 0,83, 4,267 ± 1,51 e 54,2 ± 11,96. Os grupos MB e TIG apresentaram boa resistência à corrosão, com maior módulo de impedância em relação ao grupo BRA. As diferenças no pH da ...
ABSTRACT
This study evaluated and compared the electrochemical behavior of the base metal (BM) of a nickel-chromium dental alloy with welded joints obtained by brazing processes (BRA) and Tungsten Inert Gas (TIG), when immersed in artificial saliva at pH 2.5 and 5.5. Microhardness, microstructural characterization by means of optical microscopy, scanning electron microscopy (SEM) and semi-quantitative chemical analysis by Energy Dispersive Spectroscopy (EDS), were performed in the groups BM, TIG, BRA and in joints weld by laser (LAS). The BM showed a matrix rich in nickel and chromium, distributed in a typical dendritic arrangement, with inclusions of silicon and titanium, and porosities. LAS and TIG welds reveled a microstructure more refined than the BM, however, the same chemical composition and distribution of its elements. BRA showed marked differences in their microstructure, chemical composition and distribution of the elements in relation to BM. Vickers microhardness (HV), corrosion potential (Ecorr) and corrosion current density (jcorr) were statistically analyzed with ANOVA and Tukey test (p <0.05). In order to determine the influence of pH and corrosion resistance in groups BM, TIG and BRA, Student t test, with significance level of 95% was used. BM had the lowest average microhardness (HV 256.13 ± 9.39), followed by groups TIG (271.53 ± 8.07 HV), LAS (303.73 ± 13.93 HV) and BRA (551, HV 99 ± 37.73). At pH 2.5 the average Ecorr (mV) for the MB and TIG were respectively -67.9 ± 8.43 and -52.78 ± 16.74, and at pH 5.5, averaging -54, 03 ± 21.15 and -62.08 ± 20.16. LAS group showed averages of Ecorr (mV) at pH 2.5 and 5.5, respectively, -284.33 ± 19.04 and 28.96 ± -278.8. The average values of jcorr (ìA.cm-2) to BM and TIG at pH 2.5 were respectively 2.49 ± 0.95 and 5.584 ± 1.64, and at pH 5.5, 1.929 ± 0.83 and 4.267 ± 1.51. Average jcorr for LAS group (ìA.cm-2) at pH 2.5 and 5.5 were respectively 27.45 ± 4.9 and 11.96 ± 54.2. BM and TIG ...