Reparação óssea com o uso do beta fosfato tricálcico (B-tcp)® na calota craniana de ratos submetidos ao alcoolismo experimental: análises histomorfológica e histomorfométrica / Bone repair with the use of beta tricalcium phosphate (B-TCP®) in the calvarial defect of rats submitted to experimental alcoholism: histological and morphometric analysis
Bauru; s.n; 2016. 139 p. ilus, tab, graf.
Thesis em Pt | BBO | ID: biblio-867750
Biblioteca responsável: BR28.1
RESUMO
O uso crônico de etanol prejudica diretamente o processo biológico de reparo ósseo, principalmente pela inibição das células osteoblásticas, podendo causar retardo de consolidação ou pseudoartrose. Vários biomateriais naturais ou sintéticos, têm sido utilizados como uma alternativa aos enxertos ósseos. Os biomateriais sintéticos, como o Beta Fosfato Tricálcico (β-TCP) são biocompatíveis, biodegradáveis e osteocondutíveis, por orientar as células osteoblásticas, promovendo a neoformação óssea. Sendo assim, objetivou-se avaliar a influência da ingestão crônica de etanol no processo de reparo ósseo de defeitos cranianos tratados com β-TCP® comparativamente aos preenchidos com coágulo sanguíneo ea sua interferência sobre a massa corporal. Foram utilizados 40 ratos machos (Rattus norvegicus), distribuídos aleatoriamente em 2 grupos GAG – receberam água como dieta liquida, e GAL - receberam etanol a 25%. O GAL foi submetido inicialmente à adaptação gradativa ao álcool e depois permaneceu a 25% por 90dias. Após o término desse período, todos os animais foram submetidos à cirurgia experimental. Nos ossos parietais de cada animal, foram confeccionadas duas cavidades 5,0 mm de diâmetro ao lado da sutura sagital, de forma que o parietal direito foi preenchido com β-TCP® e o esquerdo com coágulo. Dessa forma, os grupos GAG e GAL foram divididos de acordo com o preenchimento dos defeitos GC-AG (Grupo Coágulo Água), GC-AL (Grupo Coágulo Álcool), GB-AG (Grupo Biomaterial Água) e GB-AL (Grupo Biomaterial Álcool). O reparo ósseo foi observado de acordo com o período de eutanásia 10, 20, 40 e 60 dias após a cirurgia. Após inclusão histológica, as peças foram submetidas à análises histomorfológica e histomorfométrica. Na análise da variação da massa corporal, observou-se que as massas iniciais do GAG foram maiores que GAL e as massas finais de GAG aumentou significativamente apenas em 60 dias e no GAL em todos os períodos...
ABSTRACT
Chronic use of ethanol directly affects the biological process of bone repair, primarily by inhibition of osteoblastic cells. This may cause delayed consolidation or nonunion.Various natural and synthetic biomaterials have been used as alternatives to bone grafting. Synthetic biomaterials such as beta tricalcium phosphate (β-TCP) are biocompatible, biodegradable, and osteoconductive, guiding osteoblastic cells and promoting bone formation. Thus, the objective was to evaluate the influence of chronic ethanol intake on the bone healing process of cranial defects treated with β-TCP® compared to those filled with blood clot. Forty male rats were used (Rattusnorvegicus), randomly divided into two groups GAG received water as a liquid diet, and GAL received 25% ethanol. The GAL group was initially subjected to gradual adaptation to the alcohol and then maintained at 25% for 90 days. At the end of this period, all animals were submitted to experimental surgery. In the parietal bone of each animal, two cavities were prepared, 5.0 mm in diameter on the side of the sagittal suture, and the right parietal was filled with β-TCP® and left to clot. Thus, the GAG and GAL groups were divided according to the filling of defects GC-AG (Clot Water Group); GC-AL (Clot Alcohol Group); GB-AG (Biomaterial Water Group); and GB-AL (biomaterial Alcohol Group). The bone repair was observed according to the euthanasia period 10; 20; 40; and 60 days after surgery. After a histological inclusion, the pieces were submitted to histomorphological and histomorphometric analysis. The histomorphological analysis was observed in the initial periods of all groups’ fibrous connective tissue filling the entire central area of the defect. The groups of defects filled with β-TCP showed tissue reaction to particles surrounded by inflammatory cells. At the end of the period of analysis, it was observed that in all groups there was little bone formation, with...
Assuntos
Palavras-chave
Texto completo: 1 Coleções: 06-national Base de dados: BBO Assunto principal: Regeneração Óssea / Fosfatos de Cálcio / Substitutos Ósseos / Alcoolismo Tipo de estudo: Evaluation_studies Limite: Animals Idioma: Pt Ano de publicação: 2016 Tipo de documento: Thesis País de publicação: Brasil
Texto completo: 1 Coleções: 06-national Base de dados: BBO Assunto principal: Regeneração Óssea / Fosfatos de Cálcio / Substitutos Ósseos / Alcoolismo Tipo de estudo: Evaluation_studies Limite: Animals Idioma: Pt Ano de publicação: 2016 Tipo de documento: Thesis País de publicação: Brasil