Estudo in vitro do padrão de crescimento e proliferação celular de pré-osteoblastos humanos com bio-oss® e genox® / In vitro study of growth and proliferation of human pre-osteoblast on bio-oss® and genox®
ROBRAC ; 26(76): 11-14, jan./mar. 2017. graf, ilus
Artigo em Português | LILACS | ID: biblio-875288
Biblioteca responsável: BR1540.9
RESUMO

Objetivo:

O presente trabalho avaliou o padrão de crescimento, o índice de proliferação celular e morfologia de pré-osteoblastos humanos cultivados com Bio-Oss® e GenOx®. Material e

Método:

Pré-osteoblastos humanos MC3T3-E1 foram cultivados em contato com os biomateriais por 1, 24 e 72horas para avaliação da proliferação celular, medido com o teste colorimétrico MTS. Para a avaliação do padrão de crescimento e da morfologia celular, as células foram cultivadas por 24 e 72 horas, respectivamente e avaliadas sob microscopia de contraste de fase e microscopia eletrônica de varredura (MEV). Para verificação de diferenças no crescimento celular entre os grupos foi utilizado o teste one-way de ANOVA, sendo considerados significantes valores de p<0,05.

Resultados:

A proliferação celular foi maior na primeira hora nas amostras em contato com os biomateriais em comparação ao grupo controle. Nos períodos de 24 e 72 horas de cultivo celular, a curva de crescimento não mostrou diferença estatisticamente significante entre os grupos (p>0.05). Na microscopia de contraste de fase observou-se que as células cresceram em proximidade aos biomateriais, iniciando a formação da monocamada de maneira semelhante. Quando analisadas no MEV, as células cultivadas sobre os biomateriais apresentaram-se com formato fusiforme e núcleo arredado.

Conclusão:

Com a comparação do comportamento biológico de Bio-Oss® e GenOx®, realizada in vitro neste estudo, pôde-se observar que apesar das diferenças físico-químicas, o padrão, índice de crescimento e morfologia celular de Bio-Oss® e GenOx® se mostraram semelhantes, e que ambos materiais são biocompatíveis e representam uma boa opção como substitutos ósseos.
ABSTRACT

Objective:

The present study aimed to evaluate the growth pattern, cell proliferation index and morphology of human preosteoblasts cultured with Bio-Oss® and GenOx®. Material and

Methods:

MC3T3-E1 human pre-osteoblasts were cultured in contact with biomaterials for 1, 24 and 72 hours for the cell proliferation assay with the colorimetric test MTS. For the growth pattern and cell morphology analysis, the cells were cultured for 24 and 72 hours, respectively, and evaluated under phase contrast microscopy and scanning electron microscopy. To verify differences in cell growth among the groups, the one-way ANOVA test was used (p <0.05).

Results:

In the first hour of cell culture the cell proliferation was pronounced in samples in contact with the biomaterials. At 24 and 72 hours of cell culture, no significant differences between the groups was observed in respect of cell proliferation. In phase contrast microscopy it was noted that the cells grew in proximity to the biomaterials, initiating the formation of a monolayer. When analyzed in the scanning electron microscopy, the cells cultured on the biomaterials presented a fusiform morphology and a round nucleus.

Conclusion:

Despite the physico-chemical differences between Bio- Oss® and GenOx®, these two biomaterials presented a similar growth index and cell morphology analysis, showing that both biomaterials are biocompatible and represent a good choice as bone substitutes.