Avaliação da resistência adesiva e características da zircônia após diferentes tratamentos de superfície / Bond strength and surface characteristics evaluation of zirconia after different treatments
São José dos Campos; s.n; 2017. 76 p. il., tab., graf..
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-906707
Biblioteca responsável: BR243.1
Localização: BR243.1; 1055. 2240
RESUMO
O objetivo desse estudo in vitro foi avaliar a resistência adesiva, rugosidade superficial, ângulo de contato e o espectro infravermelho da zircônia, após diferentes tratamentos de superfície. Para isso, blocos (n=9) de zircônia Y-TZP (e.max ZirCad - Ivoclar, Schann, Liechtenstein) foram seccionados em 39 fatias (12 x 11x 3 mm) divididas em grupos de acordo com cada teste. Para resistência adesiva, 20 fatias foram divididos em 2 grupos controle; JAT, jateamento com óxido de alumínio e sílica + primer (Monobond Plus - Ivoclar, Schann, Liechtenstein); HFP, condicionamento com ácido fluorídrico 10% + primer, e 3 experimentais PL, plasma (Plasma Não Térmico de Superfície - modelo SAP); PLP, plasma + primer; HFPLP, ácido fluorídrico + plasma + primer. Cada fatia de zircônia foi cimentada (Multilink N - Ivoclair, Schann, Liechtenstein) a um bloco pré-polimerizado de resina composta. Após a cimentação os espécimes foram seccionados, e 48 palitos com área adesiva de 1 mm2 foram obtidos em cada grupo para o ensaio de microtração (µTBS). Quatro outras fatias foram submetidas à análise de rugosidade superficial e 12 fatias submetidas à análise do ângulo de contato, após os seguintes tratamentos de superfície sem tratamento (AV), aplicação de ácido fluorídrico a 10% (AHF), aplicação de plasma (AP) e jateamento (AJ), sendo que para o ângulo de contato foram feitas medições imediatamente após o tratamento, após 12 e 24 horas. Os resultados foram submetidos à análise estatística Anova e teste de Tukey a 5% (p< 0,05). Os espectros das ligações químicas da superfície da zircônia foram determinados em 3 outras amostras após as seguintes condições sem tratamento (AV), jateamento (JAT) e aplicação de ácido fluorídrico 10% seguido da aplicação do plasma (AHFP). Em termos de adesão, não houve diferença estatística significante entre os grupos JAT e HFPLP, porém esses 2 foram estatisticamente superiores ao grupos HFP, PL e PLP. O jateamento demonstrou aumentar significantemente a rugosidade superficial em relação aos demais grupos. O plasma demonstrou diminuir o ângulo de contato da superfície da zircônia imediatamente e ao longo de 48 horas(AU)
ABSTRACT
The purpose of this in vito study was to evaluate zirconia bond strength, surface roughness, contact angle and to mesure infrared spectrum after different surface treatments. Y-TZP zirconium (e.max ZirCAD - Ivoclair, Schann, Liechtenstein) blocks (n=9) were sliced into 36 discs (12 x 11 x 3 mm) and divided (n=4) into surface treatment groups as following two control groups JAT, airborneparticle abrasion and HFP, 10% hydrofluoric acid etching + primer (Monobond Plus - Ivoclair, Schann, Liechtenstein)application ,and three experimental groups PL, non-thermal plasma (Surface Non-Thermal Plasma SAP model) application; PLP non-thermal plasma + primer application, and HFPLP, 10% hydrofluoric acid etching + non-thermal plasma + primer application. Each zirconia disk was cemented (Multilink N - Ivoclair, Schann, Liechtenstein) to a pre-polymerized resin block (Filtek Z350 - 3M, St Paul, MN, USA). After cementation the specimens were sectioned and 48 sticks with adhesive area of 1 mm2 obtained from each group for micro-tensile testing (µTBS). Four discs were submitted to surface roughness analysis and 12 discs to contact angle analysis, after the following surface treatments no treatment (AV), 10% hydrofluoric acid etching (AHF), non-thermal plasma application (AP); and airborne- particle abrasion (AJ). The results were submitted to ANOVA and Tukey's test (p < 0.05). Zirconia surface chemical bonds spectrum was determined in infrared spectroscopy for three specimens after the conditions no treatment; airborne- particle abrasion and hydrofluoric acid etching + non-thermal plasma application. The results showed no statistically significant differences between the groups JAT and HFPLP, but these two groups were statistically superior to HFP, PL and PLP. Airborne- particle abrasion resulted in a significant increase of surface roughness compared to the other groups. Non-thermal plasma was shown to decrease the contact angle of the surface, within 48 hours(AU)