Avaliação da resistência de união de cimentos endodônticos experimentais à base de MTA e butiletilenoglicol dissalicilato / Evaluation of push-out bond strength of experimental root canal sealers based on MTA and butyl ethylene glycol disalicylate
Rio de Janeiro; s.n; s.n; 2015. 56 p. tab, ilus.
Tese em Português | LILACS, BBO - Odontologia | ID: biblio-963923
Biblioteca responsável: BR1366.1
Localização: BR1366.1; 616.314, P896, TO812
RESUMO
O objetivo deste estudo foi avaliar a resistência de união de dois cimentos endodônticos experimentais à base de MTA e butiletilenoglicol dissalicilato MTAe e MTAe-HA. Os cimentos endodônticos comerciais MTA Fillapex e AH Plus foram utilizados como materiais de referência para comparação. Vinte incisivos centrais superiores permanentes humanos foram selecionados e um slice dentinário (1 ± 0,1 mm de espessura) foi obtido à partir da junção amelocementária de cada raiz. Quatro orifícios com 0,9 mm de diâmetro foram confeccionados na superfície axial de cada slice dentinário. As amostras receberam uma irrigação padronizada e foram secas com papel absorvente. Em seguida, cada um dos orifícios foi preenchido com um dos quatro cimentos endodônticos avaliados. Os slices dentinários preenchidos foram armazenados em ambiente umidificado em solução tampão fosfato-salino (pH 7,2) durante 7 dias a 37°C. Após o armazenamento, realizou-se ensaio de push-out. A carga foi aplicada com a velocidade de 0,5 mm/min até a obtenção do deslocamento do material obturador, sendo o resultado expresso em MPa. O teste de Kruskal-Wallis foi aplicado para avaliar o efeito da resistência de união de cada cimento endodôntico. O teste Mann-Whitney com correção de Bonferroni foi utilizado para isolamento das diferenças. O erro do tipo  foi fixado em 0,05. Houve diferenças estatísticas significativas entre os materiais avaliados (P = 0,000). O AH Plus demonstrou os maiores valores de resistência de união (P = 0,000). O MTA Fillapex apresentou a menor resistência de união entre todos os grupos experimentais (P = 0,000). Nenhuma diferença foi encontrada entre os dois cimentos endodônticos experimentais (P < 0,05). Pode-se concluir que os cimentos experimentais à base de MTA e butiletilenoglicol dissalicilato apresentaram resultados adequados de resistência de união à dentina quando comparados ao MTA Fillapex.
ABSTRACT
The present study was designed to investigate push-out bond strength of two experimental root canal sealers based on MTA and butyl ethylene glycol disalicylate MTAe and MTAe-HA. Commercial sealers MTA Fillapex and AH Plus were used as reference materials for comparison. Twenty human permanent maxillary central incisors were selected and one dentin slice (1 ± 0.1 mm thick) was obtained from the cementoenamel junction of each root. On the axial surface of each dentine disc, four 0.9-mm-wide holes were drilled. Standardized irrigation was performed and samples were dried with absorbent paper. Then, each role were filled with one of the four tested root canal sealers. The filled dental slices were stored in phosphate buffered saline solution (pH 7.2) for 7 days at 37°C. After storage, a push-out assessment were performed. Loading was applied at a crosshead speed of 0.5 mm/min until sealer displacement and the results were expressed in MPa. Kruskal-Wallis test was applied to assess the effect of each endodontic sealer on the push-out bond strength. Mann-Whitney with Bonferroni correction was used to isolate the differences. The alpha-type error was set at 0.05. There were significant differences among materials (P = 0.000). AH Plus filled specimens had the highest push-out bond strength values (P = 0.000). MTA Fillapex had the lowest push-out bond strength among all experimental groups (P = 0.000). No difference has been found between the two experimental root canal sealers (P < 0.05). It has been concluded that experimental MTA and butyl ethylene glycol disalicylate based sealers presented suitable dentine bond strength outcomes when compared to MTA Fillapex.
Assuntos
Texto completo: Disponível Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Materiais Restauradores do Canal Radicular / Obturação do Canal Radicular / Teste de Materiais / Colagem Dentária / Cimentos Dentários Limite: Humanos Idioma: Português Ano de publicação: 2015 Tipo de documento: Tese

Similares

MEDLINE

...
LILACS

LIS

Texto completo: Disponível Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Materiais Restauradores do Canal Radicular / Obturação do Canal Radicular / Teste de Materiais / Colagem Dentária / Cimentos Dentários Limite: Humanos Idioma: Português Ano de publicação: 2015 Tipo de documento: Tese
...