Effect of surface treatment with sandblasting and Er, Cr: YSGG laser onbonding of stainless steel orthodontic brackets to silver amalgam
Med. oral patol. oral cir. bucal (Internet)
; 17(2): 292-296, mar. 2012. ilus, tab
Artigo
em Inglês
| IBECS
| ID: ibc-98957
Biblioteca responsável:
ES1.1
Localização: BNCS
ABSTRACT
Objectives:
Satisfactory bonding of orthodontic attachments to amalgam is a challenge for orthodontists. The aim of this in vitro study was to compare the shear bond strength of stainless steel orthodontic brackets to silver amalgam treated with sandblasting and Er,CrYSGG laser. StudyDesign:
Fifty-four amalgam discs were prepared, polished and divided into three groups In group 1 (the control group) the premolar brackets were bonded using Panavia F resin cement without any surface treatment; in groups 2 and 3, the specimens were subjected to sandblasting and Er, CrYSGG laser respectively, before bracket bonding. After immersing in distilled water at 37°C for 24 hours, all the specimens were tested for shear bond strength. Bond failure sites were evaluated under a stereomicroscope. Data was analyzed using one-way ANOVA and a posthoc Tukey test.Results:
The highest and lowest shear bond strength values were recorded in the laser and control groups, respectively. There were significant differences in mean shear bond strength values between the laser and the other two groups (p<0.05). However, there were no significant differences between the sandblast and control groups(p=0.5).Conclusions:
Amalgam surface treatment with Er,CrYSGG laser increased shear bond strength of stainless steel orthodontic brackets (AU)
Buscar no Google
Coleções:
Bases de dados nacionais
/
Espanha
Base de dados:
IBECS
Assunto principal:
Aço Inoxidável
/
Contenções Ortodônticas
/
Amálgama Dentário
/
Lasers de Estado Sólido
Limite:
Humanos
Idioma:
Inglês
Revista:
Med. oral patol. oral cir. bucal (Internet)
Ano de publicação:
2012
Tipo de documento:
Artigo
Instituição/País de afiliação:
Tabriz University of Medical Sciences/s. p