Comportamento do titânio comercialmente puro obtido por diferentes processamentos submetidos a soluções fluoretadas / Behavior of commercially pure titanium obtained by different processing under the action of different fluoride solutions
Rio de Janeiro; s.n; 2009. 139 p. ilus, tab.
Tese em Português | LILACS, BBO - Odontologia | ID: lil-589606
Biblioteca responsável: BR1366.1
Localização: BR1366.1; 616.314, B277, TO609
RESUMO
O objetivo deste estudo in vitro foi analisar o comportamento superficial do titânio comercialmente puro (grau 2 ASTM) usinado e obtido pelo processamento de metalurgia do sob a ação de diferentes soluções fluoretadas, através da análise do grau de corrosão em microscopia óptica (MO) e da rugosidade superficial. Além disso, o estudo se propôs a comparar essas análises com os resultados obtidos com o titânio fundido da dissertação de mestrado de Barros (2004). Todas as amostras receberam procedimento metalográfico padrão e foram divididas em grupos Gr.1- saliva artificial com pH 7.0 (controle), Gr.2- gel de flúor fosfato acidulado a 1,23% com pH 3.5, Gr.3- gel de NaF a 2% com pH 6.5, Gr.4- solução de NaF a 0,05% com pH 4.0 e Gr.5- solução de NaF a 0,05% com pH 7.5. As amostras foram expostas a estas soluções por 1, 4, 8 e 16 min, intercaladas com imersão em saliva artificial por 24 h, e depois foram observadas em MO e MEV, a cada intervalo de tempo. As imagens em MO, 100x, foram classificadas através de escores de 0 a 4, conforme o grau de corrosão. A rugosidade foi analisada utilizando o parâmetro Ra. Os resultados da análise de MO foram tratados estatisticamente pelo teste qui-quadrado e da rugosidade pelo teste “F” de Snedecor e de Bonferroni (p<0,05). Nos três tipos de amostras, o Gr2 apresentou a corrosão mais severa, e os Gr.4 e 5 apresentaram os menores graus de corrosão. Entretanto, nas amostras usinadas o Gr5 apresentou uma corrosão menos acentuada em relação ao Gr4. No Gr3 houve um aumento da corrosão em função do tempo, sendo que as amostras fundidas mostraram este aumento mais rapidamente. Houve um aumento significativo na rugosidade superficial no Gr.2 nos três tipos de amostras...
ABSTRACT
The purpose of this in vitro study was to analyze the superficial behavior of commercially pure titanium (grade 2, ASTM), obtained by milling or powder metallurgical process, under the action of different fluoride solutions through the analysis of corrosion grade under an optical microscope (OM) and superficial roughness. Furthermore the results obtained from such analyses were compared with the ones of cast titanium from Barros’s master’s degree dissertation (2004). All specimens received the standard metallography procedure for titanium, and were divided into the following groups, according to the attack solution received Gr.1- synthetic saliva with pH 7.0 (control), Gr.2- 1.23% acidulated phosphate fluoride gel with pH 3.5, Gr.3- 2% NaF gel with pH 6.5, Gr.4- 0.05% NaF solution with pH 4.0, and Gr.5- 0.05% NaF solution with pH 7.5. The specimens were exposed to these solutions for 1, 4, 8, and 16 minutes, and between each of these times they were immersed in synthetic saliva for 24 h. The surfaces of samples were observed under OM and SEM at each interval time. The images of 100x in OM were classified by means of scores which ranged from 0 to 4, according to corrosion grade. The rugosity was analyzed using Ra parameter. The results of OM analysis were statistically treated by means of Chi-square test and of rugosity through Snededor “F” test and Bonferroni test (p<0,05). In the three different types of samples, the Gr2 presented the most severe corrosion, and the Gr.4 and 5 showed the smallest corrosion grade. However in the milled samples Gr5 showed a less Sharp corrosion than Gr4. The corrosion grade of Gr3 increased according to time, but the cast specimens showed this increase more quickly...