Effect of silica coating and silane surface treatment on the bond strength of soft denture liner to denture base material
J. appl. oral sci
; 21(4): 300-306, Jul-Aug/2013. tab, graf
Artigo
em Inglês
| LILACS
| ID: lil-684566
Biblioteca responsável:
BR1.1
ABSTRACT
OBJECTIVE:
This study investigated the effects of different surface treatments on the tensile bond strength of an autopolymerizing silicone denture liner to a denture base material after thermocycling. MATERIAL ANDMETHODS:
Fifty rectangular heat-polymerized acrylic resin (QC-20) specimens consisting of a set of 2 acrylic blocks were used in the tensile test. Specimens were divided into 5 test groups (n=10) according to the bonding surface treatment as follows Group A, adhesive treatment (Ufi Gel P adhesive) (control); Group S, sandblasting using 50-µm Al2O3; Group SCSIL, silica coating using 30-µm Al2O3 modified by silica and silanized with silane agent (CoJet System); Group SCA, silica coating and adhesive application; Group SCSILA, silica coating, silane and adhesive treatment. The 2 PMMA blocks were placed into molds and the soft lining materials (Ufi Gel P) were packed into the space and polymerized. All specimens were thermocycled (5,000 cycles) before the tensile test. Bond strength data were analyzed using 1-way ANOVA and Duncan tests. Fracture surfaces were observed by scanning electron microscopy. X-ray photoelectron spectrometer (XPS) and Fourier Transform Infrared spectrometer (FTIR) analysis were used for the chemical analysis and a profilometer was used for the roughness of the sample surfaces.RESULTS:
The highest bond strength test value was observed for Group A (1.35±0.13); the lowest value was for Group S (0.28±0.07) and Group SCSIL (0.34±0.03). Mixed and cohesive type failures were seen in Group A, SCA and SCSILA. Group ...
Texto completo:
Disponível
Coleções:
Bases de dados internacionais
Base de dados:
LILACS
Assunto principal:
Silanos
/
Colagem Dentária
/
Dióxido de Silício
/
Materiais Dentários
/
Bases de Dentadura
/
Reembasadores de Dentadura
Idioma:
Inglês
Revista:
J. appl. oral sci
Assunto da revista:
Odontologia
Ano de publicação:
2013
Tipo de documento:
Artigo