Implantes de titânio comercialmente puro com alta resistência mecânica para aplicações em Odontologia / High-strength, commercially pure titanium implants for dental applications
Elias, Carlos Nelson; Roestel, Jochen; Zucareli, Marco Aurélio; Campaneri, César; Resende, Celso R. S.
Afiliação
  • Elias, Carlos Nelson; Instituto Militar de Engenharia. BR
  • Roestel, Jochen; Universidade Natal-África do Sul. BR
  • Zucareli, Marco Aurélio; Escola Politécnica. BR
  • Campaneri, César; Universidade Federal de São Carlos. BR
  • Resende, Celso R. S; Instituto Militar de Engenharia. BR
ImplantNews ; 10(6a): 74-81, 2013. ilus, tab, graf
Artigo em Português | LILACS | ID: lil-761258
Biblioteca responsável: BR243.1
RESUMO
O titânio e as suas ligas são amplamente utilizados na fabricação de implantes dentários, face a sua alta resistência à corrosão e à biocompatibilidade. No entanto, o titânio comercialmente puro (Ti cp) e a liga Ti-6Al-4V (Ti G5) têm limitações para aplicações biomédicas. A grande diferença entre os módulos de elasticidade do Ti e osso leva à transmissão indevida de forças na interface osso/implante, induzindo a ocorrência de um fenômeno denominado stress shielding. Outra limitação do Ti cp é sua baixa resistência mecânica, o que dificulta a fabricação de implantes osseointegráveis com paredes finas. A limitação do Ti G5 está associada à libertação de ions de alumínio e vanádio, os quais são tóxicos. O objetivo deste trabalho foi comparar as propriedades mecânicas e a morfologia de um novo Ti cp grau 4 (Ti G4 Hard) com o Ti cp convencional e o Ti G5. Os resultados dos ensaios mecânicos demonstraram que a resistência à tração do Ti G4 Hard é superior ao Ti cp 2, 4 e 5. A análise por microscopia eletrônica de varredura mostrou que cp Ti G4 Hard após tratamento de superfície tem características morfológicas melhores do que o Ti cp convencional e o Ti G5...
ABSTRACT
Titanium and its alloys are widely used in dental implants because they have high corrosion resistance and adequate biocompatibility. However, commercially pure titanium (cp Ti) and Ti-6Al-4V (Ti G5) have limitations for biomedical applications. The large difference between the modulus of elasticity of Ti and bone leads to improper transmission of forces in the bone-implant interface, a phenomenon called “stress shielding”. Another limitation of cp Ti is a low tensile strength, which reduces the possibility to manufacture small implants with thin walls. The limitation of Ti G5 is the release of aluminum and vanadium ions, which are toxic. The objective of this work is to compare the properties of modified cp Ti Grade 4 (Ti G4 Hard) with those of conventional cp Ti and Ti G5. The results of the mechanical tests showed that the Ti G4 Hard tensile strength is higher than for cp Ti 2, 4 and 5. Scanning electron microscopy analysis showed that cp Ti G4 Hard after surface treating has better morphological features than conventional cp Ti and Ti G5...
Assuntos
Buscar no Google
Coleções: Bases de dados internacionais Base de dados: LILACS Assunto principal: Titânio / Implantes Dentários / Osseointegração Limite: Humanos Idioma: Português Revista: ImplantNews Assunto da revista: Odontologia Ano de publicação: 2013 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Escola Politécnica/BR / Instituto Militar de Engenharia/BR / Universidade Federal de São Carlos/BR / Universidade Natal-África do Sul/BR

Similares

MEDLINE

...
LILACS

LIS

Buscar no Google
Coleções: Bases de dados internacionais Base de dados: LILACS Assunto principal: Titânio / Implantes Dentários / Osseointegração Limite: Humanos Idioma: Português Revista: ImplantNews Assunto da revista: Odontologia Ano de publicação: 2013 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Escola Politécnica/BR / Instituto Militar de Engenharia/BR / Universidade Federal de São Carlos/BR / Universidade Natal-África do Sul/BR
...