RESUMO
Titanium oxide nanopowder (TiO2 NPs) was synthesized via anodization in 0.7 M perchloric acid then annealed in nitrogen at 450 °C for 3 h to prepared the Titanium Oxide Nitrogen annealed nanoparticles (TiO2 NPs-N2) powder as catalytic support. Using a photodeposition process, gold was added with isopropanol as a sacrificial donor and H[AuCl4] acid, producing gold nanoparticles on nitrogen-annealed titanium oxide nanoparticles (Au-NPs on TiO2-NPs-N2). The mass loading of Au NPs was 2.86 × 10-4 (g/cm2). TEM images of Au NPs on TiO2-NPs-N2 suggest circular particles with a tendency to agglomerate. Cyclic voltammetry (CV) was used to investigate the electrocatalytic performance of the Au NPs/TiO2-NPs-N2 catalysts in ferrocyanide, KOH, and H2SO4, and the results were compared to those of a polycrystalline Au electrode that is readily accessible in the market. In KOH, H2SO4, and (2 M KOH + 0.1 M glycerol) solutions, the Au NPs/TiO2-NPs-N2 electrode displayed a startlingly high electrocatalytic performance. Using CV, the electrocatalytic oxygen reduction reaction (ORR) of Au NPs/TiO2-NPs-N2 and Au-NPs against glycerol oxidation in basic media was studied. The results indicated that Au NPs/TiO2-NPs-N2 is a promising support material for improving the electrocatalytic activity for acidic and basic oxidation. The electrode made of Au NPs/TiO2-NTs-N2 has steady electrocatalytic activity and may be reused repeatedly. TiO2 NPs and Au NPs/TiO2NPs-N2 showed satisfactory antibacterial activity against some human pathogenic bacteria using the disc diffusion method.