The Influence of Nitrogen Flow on the Stoichiometric Composition, Structure, Mechanical, and Microtribological Properties of TiN Coatings.

Utilizing reactive DC magnetron sputtering method, TiN coatings were deposited on the silicon substrates at different nitrogen flows and powers. A study of the X-ray phase composition of the coatings was carried out. The stoichiometric composition of the coatings was determined using energy dispersive x-ray spectroscopy. The structure of the surface, cross-section, and thickness of the coatings were determined using scanning electron (SEM) and atomic force microscopy (AFM). A significant change in the surface structure of TiN coatings was established with changes in deposition power and nitrogen flow. SEM images of cross-sections of all coated samples showed that the formation of coatings occurs in the form of a columnar structure with a perpendicular orientation relative to the silicon substrate. The mechanical properties (elastic modulus E and microhardness H) of TiN coatings of the first group demonstrate a maximum at a nitrogen flow of 3 sccm and are 184 ± 11 GPa and 15.7 ± 1.3 GPa, respectively. In the second group, the values of E and H increase due to a decrease in the size of the structural elements of the coating (grains and crystallites). In the third group, E and H decrease. Microtribological tests were carried out in 4 stages: at a constant load, multi-cycle for 10 and 100 cycles, and with increasing load. The coefficient of friction (CoF) and specific volumetric wear ω depend on the roughness, topology, and mechanical properties of the resulting coatings. Fracture toughness was determined using nanoscratch and depends on the mechanical properties of TiN coatings. Within each group, coatings with the best mechanical and microtribological properties were described: in the first group-TiN coating at 3 sccm (with (29.6 ± 0.1) at.% N), in the second group-TiN coating at 2 sccm (with (40.8 ± 0.2) at.% N), and in the third group-TiN coating at 1 sccm (c (37.3 ± 0.2) at.% N).

Properties of CrSi2 Layers Obtained by Rapid Heat Treatment of Cr Film on Silicon.

The changes in the morphology and the electrophysical properties of the Cr/n-Si (111) structure depending on the rapid thermal treatment were considered in this study. The chromium films of about 30 nm thickness were deposited via magnetron sputtering. The rapid thermal treatment was performed by the irradiation of the substrate's back side with the incoherent light flux of the quartz halogen lamps in nitrogen medium up to 200-550 °C. The surface morphology was investigated, including the grain size, the roughness parameters and the specific surface energy using atomic force microscopy. The resistivity value of the chromium films on silicon was determined by means of the four-probe method. It was established that at the temperatures of the rapid thermal treatment up to 350 °Ð¡ one can observe re-crystallization of the chromium films with preservation of the fine grain morphology of the surface, accompanied by a reduction in the grain sizes, specific surface energy and the value of specific resistivity. At the temperatures of the rapid thermal treatment from 400 to 550 °Ð¡ there originates the diffusion synthesis of the chromium disilicide CrSi2 with the wave-like surface morphology, followed by an increase in the grain sizes, roughness parameters, the specific surface energy and the specific resistivity value.

Comparative Investigations of AlCrN Coatings Formed by Cathodic Arc Evaporation under Different Nitrogen Pressure or Arc Current.

Tools and machine surfaces are subjected to various types of damage caused by many different factors. Due to this, the protecting coatings characterized by the best properties for a given treatment or environment are used. AlCrN coatings with different compositions, synthesized by different methods, are often of interest to scientists. The aim of the presented work was the deposition and investigation of two sets of coatings: (1) formed in nitrogen pressure from 0.8 Pa to 5 Pa and (2) formed at arc current from 50 A to 100 A. We study relationships between the above technological parameters and discuss their properties. Coatings formed at nitrogen pressure (pN2) up to 3 Pa crystallize both in hexagonal AlN structure and the cubic CrN structure. For pN2 > 3 Pa, they crystallize in the CrN cubic structure. Crystallite size increases with nitrogen pressure. The coatings formed at different arc currents have a cubic CrN structure and the crystallite size is independent of the current. The adhesion of the coatings is very good, independent of nitrogen pressure and arc current.

Nanomechanical and Nanotribological Properties of Nanostructured Coatings of Tantalum and Its Compounds on Steel Substrates.

The present paper addresses the problem of identification of microstructural, nanomechanical, and tribological properties of thin films of tantalum (Ta) and its compounds deposited on stainless steel substrates by direct current magnetron sputtering. The compositions of the obtained nanostructured films were determined by energy dispersive spectroscopy. Surface morphology was investigated using atomic force microscopy (AFM). The coatings were found to be homogeneous and have low roughness values (<10 nm). The values of microhardness and elastic modulus were obtained by means of nanoindentation. Elastic modulus values for all the coatings remained unchanged with different atomic percentage of tantalum in the films. The values of microhardness of the tantalum films were increased after incorporation of the oxygen and nitrogen atoms into the crystal lattice of the coatings. The coefficient of friction, CoF, was determined by the AFM method in the "sliding" and "plowing" modes. Deposition of the coatings on the substrates led to a decrease of CoF for the coating-substrate system compared to the substrates; thus, the final product utilizing such a coating will presumably have a longer service life. The tantalum nitride films were characterized by the smallest values of CoF and specific volumetric wear.

Structure and Properties of ZrON Coatings Synthesized by Cathodic Arc Evaporation.

The transition metal oxynitrides are a coating material with decorative features due to their adjustable color and good mechanical properties. The purpose of the research was to study the effect of the relative oxygen concentration O2(x) = O2/(N2 + O2) in particular on adhesion, but also on the color, structural and mechanical properties of ZrON coatings synthesized by cathodic arc evaporation on HS6-5-2 steel substrates. The surface morphology, phase and chemical composition and mechanical properties were determined using scanning electron microscopy, X-ray diffraction, wavelength dispersive X-ray spectroscopy, nanoindentation and scratch test. It was found that color of the coatings changed from light yellow for ZrN first to gold and then to graphite for Zr-O phase with increase of oxygen concentration. X-ray diffraction patterns showed that the phase separation of ZrN and ZrO2 occurred for about 35 at.% of oxygen in the coating. Increase in oxygen concentration in the coatings led to decrease in crystallite size from about 20 nm for ZrN to about 5 nm for coatings with about 35 at.% of oxygen and about 25 at.% of nitrogen. An increase in hardness from about 26 GPa for ZrN to about 30 GPa for coating with small concentration of oxygen (about 9 at.%) and then decrease to about 15 GPa was observed. Adhesion of Zr-O-N coatings demonstrated strong dependence on oxygen concentration. Critical load for ZrN is about 80 N and decreases with oxygen concentration increase to about 30 N for ZrO2.

Effect of Metallic or Non-Metallic Element Addition on Surface Topography and Mechanical Properties of CrN Coatings.

Alteration of the phase composition of a coating and/or its surface topography can be achieved by changing the deposition technology and/or introducing additional elements into the coating. Investigation of the effect of the composition of CrN-based coatings (including AlCrN and CrON) on the microparticle height and volume, as well as the construction of correlations between the friction coefficient at the microscale and the geometry of microparticles, are the goals of this study. We use atomic force microscopy (AFM), which is the most effective method of investigation with nanometer resolution. By revealing the morphology, AFM allows one to determine the diameter of the particles, their heights and volumes and to identify different phases in the studied area by contrasted properties. The evaluation of the distribution of mechanical properties (modulus of elasticity E and microhardness H) on the surfaces of multiphase coatings with microparticles is carried out by using the nanoindentation method. It is found that the roughness decreases with an increase in the Al concentration in AlCrN. For the CrON coatings, the opposite effect is observed. Similar conclusions are valid for the size of the microparticles and their height for both types of coating.

Characterization of Enamel and Dentine about a White Spot Lesion: Mechanical Properties, Mineral Density, Microstructure and Molecular Composition.

The study focuses on in vitro tracing of some fundamental changes that emerge in teeth at the initial stage of caries development using multiple approaches. The research was conducted on a mostly sound maxillary molar tooth but with a clearly visible natural proximal white spot lesion (WSL). Values of mineral density, reduced Young's modulus, indentation hardness and creep as well as the molecular composition and surface microstructure of the WSL and bordering dentine area were studied. The results obtained were compared to those of sound enamel and dentine on the same tooth. A decrease of mechanical properties and mineral density both for the WSL and bordering dentine was detected in comparison to the sound counterparts, as well as increase of creep for the enamel WSL. Differences in molecular composition and surface microstructure (including the indenter impressions) were found and described. WSL induces a serious change in the state of not only the visually affected enamel but also surrounding visually intact enamel and dentine in its vicinity. The results provide the basis for future studies of efficacy of minimal invasive treatments of caries.