Polyurethane acrylates as effective substrates for sustained in vitro culture of human myotubes.

Muscular disease has debilitating effects with severe damage leading to death. Our knowledge of muscle biology, disease and treatment is largely derived from non-human cell models, even though non-human cells are known to differ from human cells in their biochemical responses. Attempts to develop highly sought after in vitro human cell models have been plagued by early cell delamination and difficulties in achieving human myotube culture in vitro. In this work, we developed polyurethane acrylate (PUA) materials to support long-term in vitro culture of human skeletal muscle tissue. Using a constant base with modulated crosslink density we were able to vary the material modulus while keeping surface chemistry and roughness constant. While previous studies have focused on materials that mimic soft muscle tissue with stiffness ca. 12kPa, we investigated materials with tendon-like surface moduli in the higher 150MPa to 2.4GPa range, which has remained unexplored. We found that PUA of an optimal modulus within this range can support human myoblast proliferation, terminal differentiation and sustenance beyond 35days, without use of any extracellular protein coating. Results show that PUA materials can serve as effective substrates for successful development of human skeletal muscle cell models and are suitable for long-term in vitro studies. STATEMENT OF SIGNIFICANCE: We developed polyurethane acrylates (PUA) to modulate the human skeletal muscle cell growth and maturation in vitro by controlling surface chemistry, morphology and tuning material's stiffness. PUA was able to maintain muscle cell viability for over a month without any detectable signs of material degradation. The best performing PUA prevented premature cell detachment from the substrate which often hampered long-term muscle cell studies. It also supported muscle cell maturation up to the late stages of differentiation. The significance of these findings lies in the possibility to advance studies on muscle cell biology, disease and therapy by using human muscle cells instead of relying on the widely used animal-based in vitro models.

In vitro biostability of poly(dimethyl siloxane/hexamethylene oxide)-based polyurethane/layered silicate nanocomposites.

We have prepared a number of silicone-based thermoplastic polyurethane (TPU) nanocomposites and demonstrated an enhancement of in vitro biostability against metal-ion-induced oxidation for potential use in long-term implantable medical devices. Organoclays based on both low-aspect-ratio hectorites and high-aspect-ratio fluoromicas were evaluated after being dual-modified with two quaternary alkyl ammonium salts with differing degrees of polarity. The resultant nanocomposites were tested for in vitro biostability using physiologically relevant oxidizing conditions. Subsequently, the effects of oxidative treatment on the surface degradation and bulk mechanical integrity of the nanocomposites were investigated and compared with the parent TPUs to identify nanocomposites with the most desirable features for long-term implantation. Here, we demonstrate that the low-aspect-ratio organohectorite was delaminated and well dispersed in the nanocomposites. Importantly, these factors gave rise to the enhanced oxidative stability. In addition, the mechanical properties of all nanocomposites were less adversely affected by the oxidative treatment compared to their parent TPUs. These results suggest the potential for improved mechanical integrity and biostability when suitable dual modified organoclays are incorporated in a silicone-based TPU.

Organization of mixed dimethyldioctadecylammonium and choline modifiers on the surface of synthetic hectorite.

Understanding the nature of mixed surfactant self-assembly on the surface of organoclays is an important step toward optimizing their performance in polymer nanocomposites and for other potential applications, where selective surface interactions are crucial. In segmented thermoplastic polyurethane nanocomposite systems, dual-modified organoclays have shown significantly better performance compared to their single-modified counterparts. Until now, we had not fully characterized the physical chemistry of these dual-modified layered silicates, but had hypothesized that the enhanced composite performance arises due to some degree of nanoscale phase separation on the nanofiller surface, which enables enhanced compatibilization and more specific and inclusive interactions with the nanoscale hard and soft domains in these thermoplastic elastomers. This work examines the organization of quaternary alkyl ammonium compounds on the surface of Lucentite SWN using X-ray diffraction (XRD), thermogravimetric analysis (TGA), attenuated total reflectance Fourier-transfer infrared (ATR FT-IR), (13)C cross-polarization (CP)/magic angle spinning (MAS) nuclear magnetic resonance (NMR), and small-angle neutron scattering (SANS). When used in combination with choline, dimethyldioctadecylammonium (DMDO) was observed to self-assemble into discontinuous hydrophobic domains. The inner part of these hydrophobic domains was essentially unaffected by the choline (CC); however, surfactant intermixing was observed either at the periphery or throughout the choline-rich phase surrounding those domains.