Evaluation of Weldability for MAG and LASER with Galvannealed Steel.

Lower-arm, one of the components in automotive suspension module, has been fabricated by MAG welding in general which is lap jointed with 2 mm thick galvannealed steel sheet (SGAPH440). This welding process produces some problems such as significantly much spatters and weld defects of porosity in welded joint, which degrades productivity and weldability. Therefore, in order to solve these problems, this study has been tried to apply two types of solid wires with different chemical composition rate of Si and Mn, in MAG welding process. Moreover, the laser welding process has been adopted to fabricate the low-arm and compared with those of MAG welding, in terms of mechanical and metallurgical characteristics. It was observed that in MAG welded joints, much more spatters were occurred in using solid wire with higher Si and Mn contains. The maximum tensile-shear strength in laser welded joints was approximately 16.7 kN, which was almost equal to that of in MAG welded joints. The microstructure showed ferrite and martensite in weld metal in MAG and laser welded joints indicating no significantly grain size change.

The Effect of Tool Profiles on Mechanical Properties of Friction Stir Welded Al5052 T-Joints.

Al5052 T butt joints with two skins (5 mm) and one stringer (3 mm) has been successfully welded by friction stir welding (FSW). Notably, this paper has been investigated the effect of tool shape on welded formation mechanism and mechanical properties. The used shapes of tool pin are two types which are cylinder (type 1) and frustum (type 2). Dimension on two types of tool pin shape is respectively pin length of 4.7 mm and pin diameter of frustum type of top (5 mm) and bottom (3 mm). The results of experiment show that inner defects in FSWed T-joints increase significantly in accordance with traverse speed. The maximum tensile strength of welded joint fabricated using type 1 is equivalent to 85% that of the base metal, which is approximately 10% higher than that of type 2. Because welded joint of type 1 has more smoothly plastic flow in comparison with type 2. Consequently, the results show that type 1 is better appropriate for friction stir welded Al5052 T butt joints than type 2.

The functional TiO2-biodegradable plastic composite material produced by HVOF spraying process.

Photocatalytic TiO2 coatings on bio-degradable plastic(polybutylene succinate: PBS) were prepared by HVOF spraying using three kinds of agglomerated powders (P200: 200 nm, P30: 30 nm, P7: 7 nm). The microstructures of the coatings were characterized with SEM and XRD analysis, and the photocatalytic efficiency of the coatings was evaluated by photo degradation of gaseous acetaldehyde. For both the HVOF sprayed P200 and P30 coatings, high anatase ratio of 100% was achieved, regardless of the fuel gas pressure. On the other hand, for the HVOF sprayed P7 coating, the anatase ratio decreased from 100% to 49.1% with increasing fuel gas pressure. This decrease may be attributed to the much higher susceptibility to heat of the 7 nm agglomerated powders than the 30 nm and 200 nm agglomerated powders. In terms of the photocatalytic efficiency, HVOF sprayed P200 and P30 coatings seemed to outperform the P7 coatings because of their higher anatase ratios. However, the HVOF sprayed P7 coatings did not show photocatalytic activity possibly because of the extremely small reaction surface area to the photo-catalytic activity and low anatase ratio. Therefore, the present study found that functional PBS plastic with photocatalytic performance could be produced by spraying of ceramics such as TiO2.

Interdiffusion of Al-Ni system enhanced by ultrasonic vibration at ambient temperature.

At ambient temperature, Al-1%Si wire of 25 microm diameter was bonded successfully onto the Au/Ni/Cu pad by ultrasonic wedge bonding technology. Physical process of the bond formation and the interface joining essence were investigated. It is found that the wire was softened by ultrasonic vibration, at the same time, pressure was loaded on the wire and plastic flow was generated in the bonding wire, which promoted the diffusion for Ni into Al. Ultrasonic vibration enhanced the interdiffusion that resulted from the inner defects such as dislocations, vacancies, voids and so on, which ascribed to short circuit diffusion.