RESUMO
Iron oxide nanoparticles (IONPs) have been extensively explored in biomedicine, bio-sensing, hyperthermia, and drug/gene delivery, attributed to their versatile and tunable properties. However, owing to its numerous applications, the functionalization of IONPs with appropriate materials is in demand. To achieve optimal functionalization of IONPs, polydopamine (PDA) was utilized due to its ability to provide a superior functionalized surface, near-infrared light absorption, and adhesive nature to customize desired functionalized IONPs. This notion of involving PDA led to the successful synthesis of magnetite-PDA nanoparticles, where PDA is surface-coated on magnetite (Fe3O4@PDA). The Fe3O4@PDA nanoparticles were characterized using techniques like TEM, FESEM, PXRD, XPS, VSM, and FTIR, suggesting PDA's successful attachment with magnetite crystal structure retention. Human serum albumin (HSA), the predominant protein in blood plasma, interacts with the delivered nanoparticles. Therefore, we have employed various spectroscopic techniques, along with cytotoxicity, to inspect the effect of Fe3O4@PDA NPs on the stability and structure of HSA. The structural alterations were examined using circular dichroism (CD) and synchronous fluorescence spectroscopy (SFS). It has been observed that there are no structural perturbations in the secondary structure of the HSA protein after interaction with Fe3O4@PDA. Studies using steady-state fluorescence revealed that the inherent fluorescence intensities of HSA were suppressed after interaction with Fe3O4@PDA. In addition, temperature-dependent fluorescence measurements suggested that the type of quenching consists of both static and dynamic quenching simultaneously. A cytotoxicity study in Drosophila melanogaster larvae revealed no cytotoxic effects but did show a minor genotoxic effect only at higher concentrations.
RESUMO
This work aims to demonstrate the effect of ZrO2 and MgO inclusion into the Poly(methyl methacrylate) (PMMA). To fabricate novel hybrid composites via heat cure method, various composites (PZM2, PZM4 and PZM6) were synthesized in the system [(95-x) PMMA + 5 ZrO2 + x MgO] (x = 2, 4, and 6) respectively. Density of the prepared composites were determined and varying between 1.035-1.152 g/cm3. X-ray Diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) followed by EDAX and mechanical testing were performed to evaluate the fabricated composite properties. Moreover, to explore the structure of the fabricated composites the 13 C CP-MAS SSNMR and 1 H-13 C Phase-Modulated Lee Goldberg (PMLG) HETCOR Spectrum were recorded which clarify chemical shifting and motional dynamics of the composites. Mechanical tests were performed by UTM and the obtained parameters such as compressive strength, Young's modulus, fracture toughness, brittleness coefficient, flexural strength and flexural modulus are found to be in the range of 91-100 MPa, 0.48-0.51 GPa, 9.122-9.705 MPa.m1/2, 0.66-0.815, 51.03-42.78 MPa and 499-663 MPa respectively. Some more mechanical parameters such as proportional limit, elastic limit, failure strength, modulus of resilience and modulus of toughness were also calculated. Furthermore, tribological properties were also determined and the coefficient of friction (COF) was decreased by 17.4 % and 38 % for composite PZM6 at 20 N and 40 N as compared to the composite PZM2 and the lowest wear volume of 1.55 mm3 was observed for PZM2, whereas the maximum volume loss of 5.64 mm3 is observed for composite PZM6. To check out the biocompatibility, cytotoxicity and genotoxicity of the fabricated composites the Trypan-blue assay was also performed for PZM2 and PZM6 composites. Dissection on the gut of larvae was also performed on the both composites followed by DAPI and DCFH-DA staining. Therefore, these synthesized samples can be used for the fabrication of denture materials.