Influence of Fiber Deviation on Strength of Thin Birch (Betula pendula Roth.) Veneers.

The currently pursued implementation of wood into novel high performance applications such as automotive parts require knowledge about the material behaviour including ultimate strength. Previous research has shown that fiber deviation seems to be the dominating factor influencing the strength of thin veneers. This study aims to further investigate and quantify the influence of fiber deviation in two dimension and different hierarchical levels on the tensile strength of thin birch veneers. The fiber deviation in- and out-of-plane as well as the micro fibril angle were assessed by means of wide-angle X-ray scattering. Tensile strength was determined in laboratory experiments. Results show a high variability for in-plane fiber deviation mainly constituted by knots and other growth influencing factors. Pearson correlations between strength and fiber deviation ranged from -0.594 up to -0.852. Best correlation (r = -0.852) was achieved for maximum in-plane fiber deviation directly followed by a combined angle of in- and out-of-plane fiber deviation (r = -0.846). Based on the results it was shown that fiber deviation in- and out-of-plane is the dominating factor influencing ultimate tensile strength of thin birch veneers. Further research in regard to non-destructive strength prediction is necessary.

A new device for high-temperature in situ GISAXS measurements.

A heating stage originally designed for diffraction experiments is implemented into a Bruker NANOSTAR instrument for in situ grazing incidence small-angle x-ray scattering experiments. A controlled atmosphere is provided by a dome separating the sample environment from the evacuated scattering instrument. This dome is double shelled in order to enable cooling water to flow through it. A mesoporous silica film templated by a self-assembled block copolymer system is investigated in situ during step-wise heating in air. The GISAXS pattern shows the structural development of the ordered lattice of parallel cylindrical pores. The deformation of the elliptical pore-cross section perpendicular to the film surface was studied with increasing temperature. Moreover, the performance of the setup was tested by controlled in situ heating of a copper surface under controlled oxygen containing atmosphere.