The non-destructive investigation of a late antique knob bow fibula (Bügelknopffibel) from Kaiseraugst/CH using Muon Induced X-ray Emission (MIXE).

A knob bow fibula (Bügelknopffibel) of the Leutkirch type, which typologically belongs to the second half of the 4th and early 5th century CE, was excavated in 2018 in the Roman city of Augusta Raurica, present-day Kaiseraugst (AG, Switzerland). This was analyzed for the first time for its elemental composition by using the non-destructive technique of Muon Induced X-ray Emission (MIXE) in the continuous muon beam facility at the Paul Scherrer Institute (PSI). In the present work, the detection limit is 0.4 wt% with ∼ 1.5 hours of measurement time. The fibula was measured at six different positions, at a depth of 0.3-0.4 mm inside the material. The experimental results show that the fibula is made of bronze, containing the main elements copper (Cu), zinc (Zn), tin (Sn) and lead (Pb). The compositional similarities/differences between different parts of the fibula reveal that it was manufactured as two "workpieces". One workpiece consists of the knob (13.0±0.6 wt% Pb), bow (11.9±0.4 wt% Pb) and foot (12.5 ± 0.9 wt% Pb). These show a higher Pb content, suggesting a cast bronze. The spiral (3.2 ± 0.2 wt% Pb), which is part of the other workpiece, has a comparatively lower Pb content, suggesting a forged bronze.

Piezoelectric-driven uniaxial pressure cell for muon spin relaxation and neutron scattering experiments.

We present a piezoelectric-driven uniaxial pressure cell that is optimized for muon spin relaxation and neutron scattering experiments and that is operable over a wide temperature range including cryogenic temperatures. To accommodate the large samples required for these measurement techniques, the cell is designed to generate forces up to ∼1000 N. To minimize the background signal, the space around the sample is kept as open as possible. We demonstrate here that by mounting plate-like samples with epoxy, a uniaxial stress exceeding 1 GPa can be achieved in an active volume of at least 5 mm3. We show that for practical operation, it is important to monitor both the force and displacement applied to the sample. In addition, because time is critical during facility experiments, samples are mounted in detachable holders that can be rapidly exchanged. The piezoelectric actuators are likewise contained in an exchangeable cartridge.