NbSe2 Nanosheets/Nanorolls Obtained via Fast and Direct Aqueous Electrochemical Exfoliation for High-Capacity Lithium Storage.

Layered transition-metal dichalcogenides (LTMDs) in two-dimensional (2D) form are attractive for electrochemical energy storage, but research efforts in this realm have so far largely focused on the best-known members of such a family of materials, mainly MoS2, MoSe2, and WS2. To exploit the potential of further, currently less-studied 2D LTMDs, targeted methods for their production, preferably by cost-effective and sustainable means, as well as control over their nanomorphology, are highly desirable. Here, we report a quick and straightforward route for the preparation of 2D NbSe2 and other metallic 2D LTMDs that relies on delaminating their bulk parent solid under aqueous cathodic conditions. Unlike typical electrochemical exfoliation methods for 2D materials, which generally require an additional processing step (e.g., sonication) to complete delamination, the present electrolytic strategy yielded directly exfoliated nano-objects in a very short time (1-2 min) and with significant yields (∼16 wt %). Moreover, the dominant morphology of the exfoliated 2D NbSe2 products could be tuned between rolled-up nanosheets (nanorolls) and unfolded nanosheets, depending on the solvent where the nano-objects were dispersed (water or isopropanol). This rather unusual delamination behavior of NbSe2 was explored and concluded to occur via a redox mechanism that involves some degree of hydrolytic oxidation of the material triggered by the cathodic treatment. The delamination strategy could be extended to other metallic LTMDs, such as NbS2 and VSe2. When tested toward electrochemical lithium storage, electrodes based on the exfoliated NbSe2 products delivered very high capacity values, up to 750-800 mA h g-1 at 0.5 A g-1, where the positive effect of the nanoroll morphology, associated to increased accessibility of the lithium storage sites, was made apparent. Overall, these results are expected to expand the availability of fit-for-purpose 2D LTMDs by resorting to simple and expeditious production strategies of low environmental impact.

A Simple and Expeditious Route to Phosphate-Functionalized, Water-Processable Graphene for Capacitive Energy Storage.

Phosphate-functionalized carbon-based nanomaterials have attracted significant attention in recent years owing to their outstanding behavior in electrochemical energy-storage devices. In this work, we report a simple approach to obtain phosphate-functionalized graphene (PFG) via anodic exfoliation of graphite at room temperature with a high yield. The graphene nanosheets were obtained via anodic exfoliation of graphite foil using aqueous solutions of H3PO4 or Na3PO4 in the dual role of phosphate sources and electrolytes, and the underlying exfoliation/functionalization mechanisms are proposed. The effect of electrolyte concentration was studied, as low concentrations do not lead to a favorable graphite exfoliation and high concentrations produce fast graphite expansion but poor layer-by-layer delamination. The optimal concentrations are 0.25 M H3PO4 and 0.05 M Na3PO4, which also exhibited the highest phosphorus contents of 2.2 and 1.4 at. %, respectively. Furthermore, when PFG-acid at 0.25 M and PFG-salt at 0.05 M were tested as an electrode material for capacitive energy storage in a three-electrode cell, they achieved a competitive performance of ∼375 F/g (540 F/cm3) and 356 F/g (500 F/cm3), respectively. Finally, devices made up of symmetric electrode cells obtained using PFG-acid at 0.25 M possess energy and power densities up to 17.6 Wh·kg-1 (25.3 Wh·L-1) and 10,200 W/kg; meanwhile, PFG-salt at 0.05 M achieved values of 14.9 Wh·kg-1 (21.3 Wh·L-1) and 9400 W/kg, with 98 and 99% of capacitance retention after 10,000 cycles, respectively. The methodology proposed here also promotes a circular-synthesis process to successfully achieve a more sustainable and greener energy-storage device.

Aqueous Cathodic Exfoliation Strategy toward Solution-Processable and Phase-Preserved MoS2 Nanosheets for Energy Storage and Catalytic Applications.

The production of MoS2 nanosheets by electrochemical exfoliation routes holds great promise as a means to access this two-dimensional material in large quantities for different practical applications. However, the use of electrolytes based on synthetic organic salts and solvents, as well as issues related to the unwanted oxidation and/or phase transformation of the exfoliated nanosheets, constitute significant obstacles that hinder the industrial adoption of the electrochemical approach. Here, we introduce a safe and sustainable method for the cathodic delamination of MoS2 that makes use of aqueous solutions of very simple and widely available salts, mainly KCl, as the electrolyte. Combined with an appropriate biomolecule-based solvent transfer protocol, such an electrolytic exfoliation route is shown to afford colloidally dispersed, oxide-free, and phase-preserved MoS2 nanosheets of high structural quality in considerable yields. The mechanisms behind the efficient aqueous delamination of the bulk MoS2 cathode are also discussed and rationalized on the basis of the penetration of hydrated cations from the electrolyte between its layers and the immediate reduction of the accompanying water molecules. An asymmetric supercapacitor assembled with a cathodic MoS2 nanosheet-single walled carbon nanotube hybrid as the positive electrode and activated carbon as the negative electrode delivered energy densities (e.g., 26 W h kg-1 at 750 W kg-1 in 6 M KOH) that were competitive with those of other MoS2-based asymmetric devices. When used as a catalyst for the reduction of nitroarenes, the present cathodically exfoliated nanosheets exhibited one of the highest activities reported so far with MoS2 nanostructures, the origin of which is accounted for as well. Overall, by facilitating access to this two-dimensional material through a particularly simple, efficient, and cost-effective technique, these results should expedite the practical implementation of MoS2 nanosheets in energy storage, catalysis, and beyond.