Poly (Ionic Liquid)-Metal Organic Framework-Derived Nanoporous Carbon Membranes: Facile Fabrication and Ultrahigh Areal Capacitance.

With the rapid development of energy storage technology, the operation of portable and wearable devices is inseparable from high energy density power supplies. However, the demand for high performance supercapacitors in movable smart electronics is still restrained by their insufficient areal capacitance and limited power/energy densities. In addition, some electroactive materials, including metal oxides, conductive polymers, graphene, porous carbons, etc., are inevitable to use extra adhesives for the preparation of electrode materials. In this work, integrated hierarchical graphitic porous carbon membranes used as the electrodes without adhesives are successfully synthesized, via pyrolyzing poly(ionic liquid)s (PILs)-metal organic frameworks (MOFs) composite membranes. The asymmetric supercapacitor is assembled by the carbonized PIL-MOF composite membrane and PILs-derived porous carbon membrane, and exhibits significant areal capacitance with remarkable power and energy densities. In the two-electrode system, the areal capacitance can reach 9.5 F cm-2 with an energy density of 1.91 mWh cm-2 . In the fabricated all-solid-state supercapacitors, the areal capacitance and energy density achieved 3.2 F cm-2 and 0.65 mWh cm-2 , respectively, exceeding most reported ones. Therefore, the integrated carbon membrane electrodes with high areal capacitance reveal great potential in miniaturized devices, and further show a wider application scope through regulating PILs.

Nano-porous TiO2 layer using ultrafine nano-particles for the blocking layer in dye-sensitized solar cells.

A nano-porous TiO2 layer was produced by spray-deposition using ultrafine anatase nano-particles for the blocking layer for the dye-sensitized solar cells (DSCs). The microstructure and the electrochemical properties of the spray-deposited TiO2 layer were examined. The results of electrochemical properties showed that the spray-deposited TiO2 layer was capable to suppress the I3- ions diffusion to FTO substrate, reducing the electron recombination between the electrons on FTO substrate and I3- ions in electrolyte. In addition, the connection between TiO2 film and FTO substrate was improved by the TiO2 layer. Therefore, the short circuit current density and thereby the photo-to-electric energy conversion efficiency were improved by this blocking layer. The blocking effect of the porous layer was attributed to both the complicated pore structure of the spray-deposited layer and the enhanced connections between TiO2 film and FTO substrate. The low temperature characteristic of spray deposition approach indicates that it is suitable to the flexible-based DSCs.