Ultrasonic-assisted decoration of Ag2WO4, AgI, and Ag nanoparticles over tubular g-C3N4: Plasmonic photocatalysts for impressive removal of tetracycline under visible light.

The development of an efficient, eco-friendly, and low-cost photocatalyst is essential for addressing environmental and energy crises. In this regard, we report novel plasmonic photocatalysts through adorning tubular g-C3N4 with Ag2WO4, Ag, and AgI nanoparticles (TGCN/Ag/Ag2WO4/AgI) fabricated via a facile ultrasonic-irradiation procedure. The TGCN/Ag/Ag2WO4/AgI (20%) nanocomposite presented the excellent photocatalytic ability for removal of tetracycline hydrochloride under visible light, which was almost 45.6, 4.03, and 1.32 times more than GCN, TGCN, and TGCN/Ag/Ag2WO4 (20%) photocatalysts, respectively. Interestingly, the photocatalyst displayed impressive ability for the degradations of amoxicilline, rhodamine B, methyl orange, fuchsine, and methylene blue, which was 14.7, 52.2, 9.8, 13.2, and 7.46 times as much as pure GCN. The outcomes of DRS, PL, EIS, and photocurrent density analyses proved that the impressive activity could be related to the highly promoted harvesting of visible light, segregation of charge carriers, and improved charge migrations. In addition, trapping tests exhibited that •O2- and h+ were active species in the photocatalysis process.

Modification of PAN electrospun nanofiber membranes with g-C3N4 nanotubes/carbon dots to enhance MBR performance.

This study is dedicated to the enhancement of electrospun polyacrylonitrile (PAN) nanofiber membranes for their application in membrane bioreactor (MBR) processes. The improvement is achieved through the incorporation of graphitic carbon nitride nanotubes/carbon dots (g-C3N4 NT/CDs) and subsequent heat post-treatments at varying temperatures. Notably, the hot-pressing methodology effectively mitigates surface roughness and significantly reduces issues related to peeling during nanofiber experimentation. Our results demonstrate that the introduction of 0.5 wt% of g-C3N4 NT/CDs leads to a substantial enhancement in water flux. In particular, nanocomposite membranes subjected to hot-pressing at 90 °C for 10 min exhibited an impressive flux recovery ratio (FRR) of 70%. Furthermore, the heat-treated nanocomposite membranes exhibited remarkable antifouling properties and significantly reduced fouling rates when compared to their heat-treated bare counterparts. This study underscores the noteworthy potential of g-C3N4 NT/CDs-modified PAN nanofiber membranes to substantially elevate MBR performance, firmly positioning them as highly promising candidates for critical applications in the domains of water and wastewater treatment. However, it is imperative to underscore that the existing written material necessitates a comprehensive overhaul to align with the provided structural framework.