RESUMO
The cadmium tungstate rods have been given much attention due to their potential for usage in numerous luminescent applications. We have prepared single crystalline Sn-doped Cd1-xSnxWO4 (where x = 0, 1, 3, and 5%) nanorods (NRDs) and characterized them using refined X-ray diffraction and TEM analysis, revealing a monoclinic phase and a crystallite size that decreased from 62 to 38 nm as Sn concentration increased. Precise Sn doping modulation in CdWO4 NRDs causes surface recombination of electrons and holes, which causes the PL intensity to decrease as the Sn content rises. The chromaticity diagram shows that an increase in the Sn content caused a change in the emission color from sky blue to light green, which was attributed to the increased defect density. The photoluminescence time decay curve of all samples fit well with double-order exponential decay, and the average decay lifetime was found to be 1.11, 0.93, and 1.16 ns for Cd1-xSnxWO4, x = 0, 1, and 5%, respectively. This work provides an understanding of the behavior of Sn-doped CdWO4 NRDs during electron transitions and the physical nature of emission that could be used in bio-imaging, light sources, displays, and other applications.
Assuntos
Cádmio , Nanotubos , Luminescência , Difração de Raios XRESUMO
This study reports on the synthesis of Fe3+-activated Sr9Al6O18 nanophosphors (SAO:Fe NPs) using a simple solution combustion process, which emits a pale green light and possesses excellent fluorescence properties. An in-situ powder dusting method was utilized to extract unique ridge features of latent fingerprints (LFPs) on various surfaces using ultra-violet 254 nm excitation. The results showed that SAO:Fe NPs possess high contrast, high sensitivity, and no background interference, enabling the observation of LFPs for longer periods. Poroscopy, which is the examination of sweat pores on the skin's papillary ridges, is important in the identification process, and the YOLOv8x program based on deep convolutional neural networks was used to study the features visible in FPs. The potential of SAO:Fe NPs to ameliorate oxidative stress and thrombosis was analyzed. The results showed that SAO:Fe NPs have antioxidant properties by scavenging 2,2-diphenylpicrylhydrazyl (DPPH) and normalized the stress markers in NaNO2-induced oxidative stress in Red Blood Cells (RBC). In addition, SAO:Fe inhibited platelet aggregation induced by adenosine diphosphate (ADP). Therefore, SAO:Fe NPs may have potential applications in advanced cardiology and forensic sciences. Overall, this study highlights the synthesis and potential applications of SAO:Fe NPs, which can enhance the sensitivity and specificity of fingerprint detection and provide insights into developing novel treatments for oxidative stress and thrombosis.