Evaluation of Single-Shade Composite Resin Color Matching on Extracted Human Teeth.

Introduction: Universal single-shade composite resins are characterized by a property that enables the creation of restorations that mimic tooth structure to the extent possible with fewer shades of color. Objectives: This study aimed to instrumentally and visually evaluate the color correspondence of two single-shade composite resins in extracted human teeth multishade composite resins. Methods: Upper central incisors and upper and/or lower molars with intact buccal surfaces were selected. The study consisted of a control group (n = 20): Z250 XT (3M ESPE) (G1) multishade composite resin in colors A1 to A4, and a test group (n = 20) divided further into two equal groups, consisting of single-shade composite resin Omnichroma (Tokuyama Dental) (G2) and single-shade composite resin Vittra APS Unique from (FGM) (G3). Instrumental evaluation was performed using a spectrophotometer, and visual evaluation was performed by three observers. Descriptive measurements related to the differences in color obtained through instrumental means were analyzed using mean and standard deviation, wherein the means were compared using ANOVA, applying the Bonferroni post hoc test. Results: A statistically significant difference was observed among the groups (G1, G2, and G3) (ANOVA: p < 0.001). For the visual assessment, regardless of the assessment group, 77.49% of the teeth were within the acceptable color-match classification, with the single-shade resins showing better correspondence than the multishade resins. Conclusion: Single-shade composite resins showed different color-matching results when compared to multishade resins, both in spectrophotometry and visual evaluations. Clinical Significance. Single-shade composite resins simplify the shade-selection process and are promising materials for use in dental practice.

Effect of dentin pretreatment with potassium oxalate: A 6-year follow-up.

Oxalate-based products are effective against dentine sensitivity and have been studied as an option to improve long-term adhesive bonding strength. Our aim was to evaluate the effect of potassium oxalate on the microtensile bond strength (µTBS) of the dentin/resin interface after 24 h, 1, and 6 years. Dentin on the occlusal surface of 16 human premolars was exposed and etched with 35% phosphoric acid. The teeth were divided into four groups. Two groups received 3% monohydrated potassium oxalate and the following adhesive systems and composites: Adper Scotchbond Multipurpose + FiltekZ350 (3M/ESPE) and Prime & Bond NT + Esthet-X (Dentsply). Two control groups did not receive potassium oxalate. Teeth were cut into sticks and kept in distilled water at 37°C for 24 h, 1, and 6 years. The sticks underwent µTBS testing after storage. ANOVA, Tukey's post hoc test, and paired t test were used to compare storage times (α = 0.05). The fracture mode of the specimens was classified under a stereomicroscope (40×). Morphology of the hybrid layer and the fracture pattern were observed with scanning electronic microscopy (SEM). Mean µTBS was high at 24 h and decreased after 1 and 6 years. After 6 years, the mean µTBS values were similar with no statistically significant difference between the groups (p = .121). SEM images showed proper dentin hybridization. Dentin pretreatment with potassium oxalate did not affect hybrid layer formation, but bond strength decreased over time after 24 h. Therefore, the clinical use of potassium oxalate to increase dentin bond durability is not indicated.