Influence of Specimen Dimension, Water Immersion Protocol, and Surface Roughness on Water Sorption and Solubility of Resin-Based Restorative Materials.

The evaluation of water sorption and solubility is pivotal for the development of new resin-based restorative materials with the potential for clinical application. The purpose of the present study was to evaluate the influence of the specimen dimension, water immersion protocol, and surface roughness on the water sorption and solubility of three resin-based restorative materials. Disk-shaped specimens of 15 mm × 1 mm, 10 mm × 1 mm, and 6 mm × 1 mm were produced with a composite resin (Z100), a resin cement (RelyX ARC), and an adhesive system (Single Bond 2-SB2). The specimens were immersed in distilled water according to four protocols: ISO (all the specimens for each group were vertically immersed in 50 mL); IV-10 (the specimens were individually and vertically immersed in 10 mL); IH-10 (the specimens were individually and horizontally immersed in 10 mL); and IH-2 (the specimens were individually and horizontally immersed in 2 mL). The surface roughness (Sa and Sp) was evaluated using an atomic force microscope, and the degree of conversion was determined using FT-IR spectrometry. The specimen dimension and water immersion protocol had no effect on water sorption and solubility. For the three resin-based restorative materials, Sp was higher than Sa. The degree of conversion was not influenced by the specimen dimension. The variations in the specimen dimension and water immersion protocol compared to those determined by ISO 4049 did not prevent the comparison between the values of water sorption and solubility obtained for a given resin-based restorative material.

Fabrication and characterization of remineralizing dental composites containing hydroxyapatite nanoparticles.

The aim of this study was to fabricate and characterize dental composites containing hydroxyapatite nanoparticles (HApNPs). Four dental composites were produced from the same organic matrix (70 wt% Bis-GMA and 30 wt% TEGDMA), with partial replacement of BaBSi particles (65 wt%) by HApNPs in the following concentrations (wt%): E0 (0) - control, E10 (10), E20 (20) and E30 (30). Ca2+ and PO43- release was evaluated in solutions with different pHs (4, 5.5, and 7) using atomic emission spectroscopy with microwave-induced nitrogen plasma while the enamel remineralization potential was evaluated in caries-like enamel lesions induced by S. mutans biofilm using micro-CT. The following properties were characterized: degree of conversion (DC%), microhardness (KHN), flexural strength (FS), elastic modulus (EM) and translucency (TP). The higher the HApNPs content, the higher the Ca2+ and PO43- release. The ions release was influenced by pH (4 > 5.5 > 7) (p < 0.05). All composites loaded with HApNPs were able to remineralize the enamel (E30 = E20 > E10) (p < 0.05). Contrarily, E0 was not able of recovering the enamel mineral loss. E0 and E10 presented highest DC%, while E20 and E30 showed similar and lowest DC%. KHN and FS were decreased with the addition of HApNPs, while EM was not influenced by the incorporation of HApNPs. E10 presented statistically similar TP to E0, while this property decreased for E20 and E30 (p < 0.05). Incorporation of HApNPs into dental composites promoted enamel remineralization, mainly at potentially cariogenic pH (= 4), while maintained their overall performance in terms of physicomechanical properties.

Condicionamento ácido em dentina: comparaçäo entre ácidos e jateamento com óxido de silício / Dentin etching: comparative study between acids and Sio2 treatment

Os autores estudaram a efetividade dos ácidos indicados pelos fabricantes para condicionar esmalte e dentina e sua efetividade na dentina, comparando-o com o tratamento por meio de jateamento de óxido de silício (Sio2) em dentes recém-extraídos. As coroas dos dentes foram preparadas para expor a dentina na junçäo amelo-dentinária e os ácidos aplicados conforme recomendados pelos fabricantes. As dentinas condicionadas foram preparadas para visualizaçäo em microscopia eletrônica de varredura, com aumentos de 500 a 1.000 vezes. Os ácidos foram analisados quimicamente e comparados com as especificaçöes dos fabricantes. Os resultados mostraram a efetividade do ácido fosfórico a 37 por cento na limpeza do smear layer e smear plug e do tratamento da dentina com jatos de óxido de silício