Effect of different electrolytes and deposition time on the supercapacitor properties of nanoflake-like Co(OH)2 electrodes.

The effect of ultrasonic treatment and deposition time on nanoflake-like Co(OH)2 thin films were prepared using the potentiostatic mode of electrodeposition method on stainless steel substrates by a nitrate reduction reaction. After ultrasonic treatment, we used stainless steel substrates for deposition of the nanoflakes like Co(OH)2 thin films. The effect of deposition times and electrolytes on different physico-chemical properties of Co(OH)2 was investigated in detail, such as X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), and electrochemical testing. After ultrasonic treatment Co(OH)2 thin films had devolvement of the uniform and interconnected formation of nanoflakes nanostructures. Supercapacitor performance of the Co(OH)2 electrodes suggest that, specific capacitance are depends on the surface morphology, and Co(OH)2 electrodes after ultrasonic treatment exhibited higher performance than without ultrasonication. The maximum specific capacitance of the 30 min. deposited Co(OH)2 nanoflakes exceeded 276 Fg-1 in 0.5M KOH electrolyte at 5 mVs-1 scan rate.

Nanorods to hexagonal nanosheets of CuO-doped manganese oxide nanostructures for higher electrochemical supercapacitor performance.

In this work, the extraordinary properties of CuO addition on the morphology and supercapacitive performance of Mn2O3 electrodes were demonstrated. Concisely, CuO/Mn2O3 thin films were prepared by an easy and inexpensive successive ionic layer adsorption and reaction (SILAR) method. The prepared thin films were characterized by various sophisticated physiochemical systems. The results demonstrated formation of Mn2O3 thin films with noteworthy morphological alteration upon introduction of CuO. Furthermore, a significant effect of CuO introduction was observed on the electrocatalytic properties of the nanostructured Mn2O3 electrodes. At 3% CuO doping, the Mn2O3 electrodes displayed the maximum specific capacitance owing to formation of nanoplate-like structures. The enhanced specific capacitance attained for 3% CuO doping in the Mn2O3 electrode was 500 F/g at 5 mV/s in a 3 M KOH electrolyte. All results confirmed the plausible potential of the CuO/Mn2O3 electrode for supercapacitor applications.

Morphological enhancement to CuO nanostructures by electron beam irradiation for biocompatibility and electrochemical performance.

This paper reports the effect of electron beam irradiation on CuO thin films synthesized by the successive ionic layer adsorption and reaction (SILAR) method on copper foil for supercapacitor and biocompatibility application. Pristine and irradiated samples were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, and electrochemical study. Pristine and irradiated CuO films were pure monoclinic phase, with uniform nanostructures over the whole copper foil. After irradiation, CuO samples had formed innovative nanostructures. Biocompatibility of pristine and irradiated CuO samples suggest that CuO sample is non-toxic and ecofriendly. The specific capacitance of pristine and irradiated CuO strongly depends on surface morphology, and CuO electrodes after irradiation showed superior performance than pristine CuO. The highest specific capacitance of the 20kGy irradiated CuO nanoflowers exceeded 511Fg-1 at 10mVs-1 in 1M KOH electrolyte. Irradiated CuO samples also showed lower ESR, and were superior to other report electrical energy storage materials.

Chemical synthesis of hierarchical NiCo2S4 nanosheets like nanostructure on flexible foil for a high performance supercapacitor.

In this study, hierarchical interconnected nickel cobalt sulfide (NiCo2S4) nanosheets were effectively deposited on a flexible stainless steel foil by the chemical bath deposition method (CBD) for high-performance supercapacitor applications. The resulting NiCo2S4 sample was characterized by X-ray powder diffraction (XRD), field emission scanning electron microscopy (FE-SEM), high-resolution transmission electron microscopy (HR-TEM), and electrochemical measurements. XRD and X-ray photoelectron spectroscopy (XPS) results confirmed the formation of the ternary NiCo2S4 sample with a pure cubic phase. FE-SEM and HR-TEM revealed that the entire foil surface was fully covered with the interconnected nanosheets like surface morphology. The NiCo2S4 nanosheets demonstrated impressive electrochemical characteristics with a specific capacitance of 1155 F g-1 at 10 mV s-1 and superior cycling stability (95% capacity after 2000 cycles). These electrochemical characteristics could be attributed to the higher active area and higher conductivity of the sample. The results demonstrated that the interconnected NiCo2S4 nanosheets are promising as electrodes for supercapacitor and energy storage applications.

Chemical synthesis of flower-like hybrid Cu(OH)2/CuO electrode: Application of polyvinyl alcohol and triton X-100 to enhance supercapacitor performance.

In this research article, we report hybrid nanomaterials of copper hydroxide/copper oxide (Cu(OH)2/CuO). A thin films were prepared by using a facile and cost-effective successive ionic layer adsorption and reaction (SILAR) method. As-synthesized and hybrid Cu(OH)2/CuO with two different surfactants polyvinyl alcohol (PVA) and triton-X 100 (TRX-100) was prepared having distinct morphological, structural, and supercapacitor properties. The surface of the thin film samples were examined by scanning electron microscopy (SEM). A nanoflower-like morphology of the Cu(OH)2/CuO nanostructures arranged vertically was evidenced on the stainless steel substrate. The surface was well covered by nanoflake-like morphology and formed a uniform Cu(OH)2/CuO nanostructures after treating with surfactants. X-ray diffraction patterns were used to confirm the hybrid phase of Cu(OH)2/CuO materials. The electrochemical properties of the pristine Cu(OH)2/CuO, PVA:Cu(OH)2/CuO, TRX-100:Cu(OH)2/CuO films were observed by cyclic voltammetry, galvanostatic charge/discharge, and electrochemical impedance spectroscopy technique. The electrochemical examination reveals that the Cu(OH)2/CuO electrode has excellent specific capacitance, 292, 533, and 443Fg-1 with pristine, PVA, and TRX-100, respectively in 1M Na2SO4 electrolyte solution. The cyclic voltammograms (CV) of Cu(OH)2/CuO electrode shows positive role of the PVA and TRX-100 to enhance supercapacitor performance.