Mechanistically Guided Materials Chemistry: Synthesis of Ternary Nitrides, CaZrN2 and CaHfN2.

Recent computational studies have predicted many new ternary nitrides, revealing synthetic opportunities in this underexplored phase space. However, synthesizing new ternary nitrides is difficult, in part because intermediate and product phases often have high cohesive energies that inhibit diffusion. Here, we report the synthesis of two new phases, calcium zirconium nitride (CaZrN2) and calcium hafnium nitride (CaHfN2), by solid state metathesis reactions between Ca3N2 and MCl4 (M = Zr, Hf). Although the reaction nominally proceeds to the target phases in a 1:1 ratio of the precursors via Ca3N2 + MCl4 → CaMN2 + 2 CaCl2, reactions prepared this way result in Ca-poor materials (CaxM2-xN2, x < 1). A small excess of Ca3N2 (ca. 20 mol %) is needed to yield stoichiometric CaMN2, as confirmed by high-resolution synchrotron powder X-ray diffraction. In situ synchrotron X-ray diffraction studies reveal that nominally stoichiometric reactions produce Zr3+ intermediates early in the reaction pathway, and the excess Ca3N2 is needed to reoxidize Zr3+ intermediates back to the Zr4+ oxidation state of CaZrN2. Analysis of computationally derived chemical potential diagrams rationalizes this synthetic approach and its contrast from the synthesis of MgZrN2. These findings additionally highlight the utility of in situ diffraction studies and computational thermochemistry to provide mechanistic guidance for synthesis.

"Mn3AlN" is Really Mn4N.

We investigate the synthesis of antiperovskite "Mn3AlN" using the published synthesis procedure, as well as several new reaction pathways. In each case, only a combination of antiperovskite Mn4N and Mn5Al8 or precursors is obtained. The identity of the obtained antiperovskite phase is unambiguously determined to be Mn4N via synchrotron powder X-ray diffraction (SPXRD), X-ray absorption spectroscopy (XAS), and magnetometry. The experimental results are further supported by thermochemical calculations informed by density functional theory (DFT), which find Mn3AlN to be metastable versus decomposition into Mn and AlN. The DFT-based calculations also predict an antiferromagnetic ground state for Mn3AlN. This directly contradicts the previously reported ferromagnetic behavior of "Mn3AlN". Instead, the observed magnetic behavior is consistent with ferrimagnetic Mn4N. We examine the data in the original publication and conclude that the compound reported to be Mn3AlN is in fact Mn4N.

Selective Synthesis of Defect-Rich LaMnO3 by Low-Temperature Anion Cometathesis.

The synthesis of complex oxides at low temperatures brings forward aspects of chemistry not typically considered. This study focuses on perovskite LaMnO3, which is of interest for its correlated electronic behavior tied to the oxidation state and thus the spin configuration of manganese. Traditional equilibrium synthesis of these materials typically requires synthesis reaction temperatures in excess of 1000 °C, followed by subsequent annealing steps at lower temperatures and different p(O2) conditions to manipulate the oxygen content postsynthesis (e.g., LaMnO3+x). Double-ion exchange (metathesis) reactions have recently been shown to react at much lower temperatures (500-800 °C), highlighting a fundamental knowledge gap for how solids react at lower temperatures. Here, we revisit the metathesis reaction, LiMnO2 + LaOX, where X is a halide or mixture of halides, using in situ synchrotron X-ray diffraction. These experiments reveal low reaction onset temperatures (ca. 450-480 °C). The lowest reaction temperatures are achieved by a mixture of lanthanum oxyhalide precursors: 2 LiMnO2 + LaOCl + LaOBr. In all cases, the resulting products are the expected alkali halide salt and defective La1-ϵMn1-ϵO3, where ϵ = x/(3 + x). We observe a systematic variation in defect concentration, consistent with a rapid stoichiometric local equilibration of the precursors and the subsequent global thermodynamic equilibration with O2 (g), as revealed by computational thermodynamics. Together, these results reveal how the inclusion of additional elements (e.g., Li and a halide) leads to the local equilibrium, particularly at low reaction temperatures for solid-state chemistry.

Two-Step Solid-State Synthesis of Ternary Nitride Materials.

Ternary nitride materials hold promise for many optical, electronic, and refractory applications; yet, their preparation via solid-state synthesis remains challenging. Often, high pressures or reactive gases are used to manipulate the effective chemical potential of nitrogen, yet these strategies require specialized equipment. Here, we report on a simple two-step synthesis using ion-exchange reactions that yield rocksalt-derived MgZrN2 and Mg2NbN3, as well as layered MgMoN2. All three compounds show almost temperature-independent and weak paramagnetic responses to an applied magnetic field at cryogenic temperatures, indicating phase-pure products. The key to synthesizing these ternary materials is an initial low-temperature step (300-450 °C) to promote Mg-M-N nucleation. The intermediates then are annealed (800-900 °C) to grow crystalline domains of the ternary product. Calorimetry experiments reveal that initial reaction temperatures are determined by phase transitions of reaction precursors, whereas heating directly to high temperatures results in decomposition. These two-step reactions provide a rational guide to material discovery of other bulk ternary nitrides.

Pregnancy and Childbirth: A Cochrane Pocketbook

Pregnancy and Childbirth presents the best evidence for the care of pregnant women to doctors, midwives, students and parents. The logical sequence of chapters and the index give quick access to the abstracts of over four hundred Cochrane systematic reviews. The book serves both as a stand-alone reference, and as a companion to locating full reviews on the Cochrane Library.