RESUMO
Ferromagnetic La0.7Sr0.3Mn1-xRuxO3 epitaxial multilayers with controlled variation of the Ru/Mn content were synthesized to engineer canted magnetic anisotropy and variable exchange interactions, and to explore the possibility of generating a Dzyaloshinskii-Moriya interaction. The ultimate aim of the multilayer design is to provide the conditions for the formation of domains with nontrivial magnetic topology in an oxide thin film system. Employing magnetic force microscopy and Lorentz transmission electron microscopy in varying perpendicular magnetic fields, magnetic stripe domains separated by Néel-type domain walls as well as Néel skyrmions smaller than 100 nm in diameter were observed. These findings are consistent with micromagnetic modeling, taking into account a sizable Dzyaloshinskii-Moriya interaction arising from the inversion symmetry breaking and possibly from strain effects in the multilayer system.
RESUMO
Magnetic skyrmions are topologically protected spin textures that exhibit fascinating physical behaviours and large potential in highly energy-efficient spintronic device applications. The main obstacles so far are that skyrmions have been observed in only a few exotic materials and at low temperatures, and fast current-driven motion of individual skyrmions has not yet been achieved. Here, we report the observation of stable magnetic skyrmions at room temperature in ultrathin transition metal ferromagnets with magnetic transmission soft X-ray microscopy. We demonstrate the ability to generate stable skyrmion lattices and drive trains of individual skyrmions by short current pulses along a magnetic racetrack at speeds exceeding 100 m s(-1) as required for applications. Our findings provide experimental evidence of recent predictions and open the door to room-temperature skyrmion spintronics in robust thin-film heterostructures.