Nanoselective area growth (NSAG) by metal organic vapor phase epitaxy of high-quality InGaN nanopyramids on GaN-coated ZnO/c-sapphire is reported. Nanopyramids grown on epitaxial low-temperature GaN-on-ZnO are uniform and appear to be single crystalline, as well as free of dislocations and V-pits. They are also indium-rich (with homogeneous 22% indium incorporation) and relatively thick (100 nm). These properties make them comparable to nanostructures grown on GaN and AlN/Si templates, in terms of crystallinity, quality, morphology, chemical composition and thickness. Moreover, the ability to selectively etch away the ZnO allows for the potential lift-off and transfer of the InGaN/GaN nanopyramids onto alternative substrates, e.g. cheaper and/or flexible. This technology offers an attractive alternative to NSAG on AlN/Si as a platform for the fabrication of high quality, thick and indium-rich InGaN monocrystals suitable for cheap, flexible and tunable light-emitting diodes.
RESUMO
We report improved sensitivity to NO, NO2 and NH3 gas with specially-designed AlGaN/GaN high electron mobility transistors (HEMT) that are suitable for operation in the harsh environment of diesel exhaust systems. The gate of the HEMT device is functionalized using a Pt catalyst for gas detection. We found that the performance of the sensors is enhanced at a temperature of 600 °C, and the measured sensitivity to 900 ppm-NO, 900 ppm-NO2 and 15 ppm-NH3 is 24%, 38.5% and 33%, respectively, at 600 °C. We also report dynamic response times as fast as 1 s for these three gases. Together, these results indicate that HEMT sensors could be used in a harsh environment with the ability to control an anti-pollution system in real time.
RESUMO
Metal-semiconductor-metal (MSM) detectors based on Ti/Au and Ni/Au interdigitated structures were fabricated using 2.5 micrometer thick hexagonal boron nitride (h-BN) layer with both natural and 10B-enriched boron. Current-voltage (I-V) and current-time (I-t) curves of the fabricated detectors were recorded with (I N) and without (I d) neutron irradiation, allowing the determination of their sensitivity (S = (I N - I d)/I d = ΔI/I d). Natural and 10B-enriched h-BN detectors exhibited high neutron sensitivities of 233 and 367% at 0 V bias under a flux of 3 × 104 n/cm2/s, respectively. An imbalance in the distribution of filled traps between the two electric contacts could explain the self-biased operation of the MSM detectors. Neutron sensitivity is further enhanced with electrical biasing, reaching 316 and 1192% at 200 V and a flux of 3 × 104 n/cm2/s for natural and 10B-enriched h-BN detectors, respectively, with dark current as low as 2.5 pA at 200 V. The increased performance under bias has been attributed to a gain mechanism based on neutron-induced charge carrier trapping at the semiconductor/metal interface. The response of the MSM detectors under thermal neutron flux and bias voltages was linear. These results clearly indicate that the thin-film monocrystal BN MSM neutron detectors can be optimized to operate sensitively with the absence of external bias and generate stronger signal detection using 10B-enriched boron.
RESUMO
(1) Backround: Technological advances should foster gains in physicians' efficiency. For example, a reduction of the medical decision time can be enabled by faster biological tests. The main objective of this study was to collect responses from an international panel of physicians on their needs for biomarkers and also to convey the improvement in the outcome to be made possible by the potential development of fast diagnostic tests for these biomarkers. (2) Methods: we distributed a questionnaire on the Internet to physicians. (3) Results: 508 physicians participated in this survey. The mean age was 38 years. General practice and emergency medicine were heavily represented, with 95% CIs of 44% (39.78, 48.41) and 32% (27.84, 35.94)), respectively. The two most represented countries were France (95% CI: 74% (70.20, 77.83)) and the USA (95% CI: 11% (8.65, 14.18)). Ninety-eight percentages of the physicians thought that obtaining cited biomarkers more quickly would be beneficial to their practice and to patient's care. The main biomarkers of interest identified by our panel were troponin (95% CI: 51% (46.24, 54.94)), C-reactive protein (95% CI: 42% (38.03, 46.62)), D-dimer (95% CI: 29% (24.80, 32.68)), and brain natriuretic peptide (95% CI: 13% (10.25, 16.13)). (4) Conclusions: Our study highlights the real technological need for fast biomarker results, which could be provided by biosensors. The relevance of some answers such as troponin is questionable.
RESUMO
We have previously surveyed a panel of 508 physicians from around the world about which biomarkers would be relevant if obtained in a very short time frame, corresponding to emergency situations (life-threatening or not). The biomarkers that emerged from this study were markers of cardiovascular disease: troponin, D-dimers, and brain natriuretic peptide (BNP). Cardiovascular disease is a group of disorders affecting the heart and blood vessels. At the intersection of medicine, basic research and engineering, biosensors that address the need for rapid biological analysis could find a place of choice in the hospital or primary care ecosystem. Rapid, reliable, and inexpensive analysis with a multi-marker approach, including machine learning analysis for patient risk analysis, could meet the demand of medical teams. The objective of this opinion review, proposed by a multidisciplinary team of experts (physicians, biologists, market access experts, and engineers), is to present cases where a rapid biological response is indeed valuable, to provide a short overview of current biosensor technologies for cardiac biomarkers designed for a short result time, and to discuss existing market access issues.
RESUMO
Reliable p-doped hexagonal boron nitride (h-BN) could enable wide bandgap optoelectronic devices such as deep ultra-violet light emitting diodes (UV LEDs), solar blind photodiodes and neutron detectors. We report the study of Mg in h-BN layers as well as Mg h-BN/AlGaN heterostructures. Mg incorporation in h-BN was studied under different biscyclopentadienyl-magnesium (Cp2Mg) molar flow rates. 2θ-ω x-ray diffraction scans clearly evidence a single peak, corresponding to the (002) reflection plane of h-BN with a full-width half maximum increasing with Mg incorporation in h-BN. For a large range of Cp2Mg molar flow rates, the surface of Mg doped h-BN layers exhibited characteristic pleats, confirming that Mg doped h-BN remains layered. Secondary ion mass spectrometry analysis showed Mg incorporation, up to 4 × 1018 /cm3 in h-BN. Electrical conductivity of Mg h-BN increased with increased Mg-doping. Heterostructures of Mg h-BN grown on n-type Al rich AlGaN (58% Al content) were made with the intent of forming a p-n heterojunction. The I-V characteristics revealed rectifying behavior for temperatures from 123 to 423 K. Under ultraviolet illumination, photocurrent was generated, as is typical for p-n diodes. C-V measurements evidence a built-in potential of 3.89 V. These encouraging results can indicate p-type behavior, opening a pathway for a new class of wide bandgap p-type layers.
RESUMO
Selective Area van der Waals Epitaxy (SAVWE) of III-Nitride device has been proposed recently by our group as an enabling solution for h-BN-based device transfer. By using a patterned dielectric mask with openings slightly larger than device sizes, pick-and-place of discrete LEDs onto flexible substrates was achieved. A more detailed study is needed to understand the effect of this selective area growth on material quality, device performance and device transfer. Here we present a study performed on two types of LEDs (those grown on h-BN on patterned and unpatterned sapphire) from the epitaxial growth to device performance and thermal dissipation measurements before and after transfer. Millimeter-size LEDs were transferred to aluminum tape and to silicon substrates by van der Waals liquid capillary bonding. It is shown that patterned samples lead to a better material quality as well as improved electrical and optical device performances. In addition, patterned structures allowed for a much better transfer yield to silicon substrates than unpatterned structures. We demonstrate that SAVWE, combined with either transfer processes to soft or rigid substrates, offers an efficient, robust and low-cost heterogenous integration capability of large-size devices to silicon for photonic and electronic applications.
RESUMO
Hexagonal boron nitride (h-BN) can be used as a p-doped material in wide-bandgap optoelectronic heterostructures or as a release layer to allow lift-off of grown three-dimensional (3D) GaN-based devices. To date, there have been no studies of factors that lead to or prevent lift-off and/or spontaneous delamination of layers. Here, we report a unique approach of controlling the adhesion of this layered material, which can result in both desired lift-off layered h-BN and mechanically inseparable robust h-BN layers. This is accomplished by controlling the diffusion of Al atoms into h-BN from AlN buffers grown on h-BN/sapphire. We present evidence of Al diffusion into h-BN for AlN buffers grown at high temperatures compared to conventional-temperature AlN buffers. Further evidence that the Al content in BN controls lift-off is provided by comparison of two alloys, Al0.03B0.97N/sapphire and Al0.17B0.83N/sapphire. Moreover, we tested that management of Al diffusion controls the mechanical adhesion of high-electron-mobility transistor (HEMT) devices grown on AlN/h-BN/sapphire. The results extend the control of two-dimensional (2D)/3D hetero-epitaxy and bring h-BN closer to industrial application in optoelectronics.
RESUMO
The transfer of GaN based gas sensors to foreign substrates provides a pathway to enhance sensor performance, lower the cost and extend the applications to wearable, mobile or disposable systems. The main keys to unlocking this pathway is to grow and fabricate the sensors on large h-BN surface and to transfer them to the flexible substrate without any degradation of the performances. In this work, we develop a new generation of AlGaN/GaN gas sensors with boosted performances on a low cost flexible substrate. We fabricate 2-inch wafer scale AlGaN/GaN gas sensors on sacrificial two-dimensional (2D) nano-layered h-BN without any delamination or cracks and subsequently transfer sensors to an acrylic surface on metallic foil. This technique results in a modification of relevant device properties, leading to a doubling of the sensitivity to NO2 gas and a response time that is more than 6 times faster than before transfer. This new approach for GaN-based sensor design opens new avenues for sensor improvement via transfer to more suitable substrates, and is promising for next-generation wearable and portable opto-electronic devices.
RESUMO
This paper is devoted to the description and characterization of a new electro-optic sensor based on a polarimetric device operating in reflection mode, and on a closed-loop controller. The main features of the proposed sensor are versatility, insensitivity to the laser beam optical power fluctuation, and fully linear working mode. The resolution of the sensor, in terms of phase shift, is shown to be better than +/-20 mrad and its accuracy to +/-50 mrad.
RESUMO
We show that a Z-transform-based time-response analysis of the electro-optical response of a crystal to a step voltage with a short rise time allows one to obtain the dispersion of the electro-optical coefficients over a wide frequency range. We describe the method employed and present the results obtained for the main electroptic coefficients (r22, r61, and rc) of a standard LiNbO3 crystal. We also show that this method is able to provide even small values of the electro-optic coefficient as well as the dispersion within a wide frequency range, which is limited only by the rise time of the step voltage.