Stable and Efficient Dye-Sensitized Solar Cells and Supercapacitors Developed Using Ionic-Liquid-Doped Biopolymer Electrolytes.

An ionic liquid (IL) 1-ethyl, 2-methyl imidazolium thiocyanate incorporated biopolymer system is reported in this communication for applications in dual energy devices, i.e., electric double-layer capacitors (EDLCs) and dye-sensitized solar cells (DSSCs). The solution caste method has been used to synthesize ionic-liquid-incorporated biopolymer electrolyte films. The IL mixed biopolymer electrolytes achieve high ionic conductivity up to the order of 10-3 S/cm with good thermal stability above 250 °C. Electrical, structural, and optical studies of these IL-doped biopolymer electrolyte films are presented in detail. The performance of EDLCs was evaluated using low-frequency electrochemical impedance spectroscopy, cyclic voltammetry, and constant current charge-discharge, while that of DSSCs was assessed using J-V characteristics. The EDLC cells exhibited a high specific capacitance of 200 F/gram, while DSSCs delivered 1.53% efficiency under sun conditions.

Alloy Disordering Effects on the Thermal Conductivity and Energy Gap Temperature Dependence of Cd1-xZnxSe Ternary Crystals Grown by the Bridgman Method.

Investigated in this work, Cd1-xZnxSe-mixed ternary compounds were grown by the Bridgman method. Several compounds with zinc content varying in the range 0 < x < 1 were produced between two binary parents, CdSe and ZnSe crystals. Using the SEM/EDS technique, the accurate composition of formed crystals was determined along the growth axis. Thanks to that, the grown crystals' axial and radial uniformity were determined. Characterization of the optical and thermal properties was undertaken. The energy gap was measured using photoluminescence spectroscopy for different compositions and temperatures. The bowing parameter describing the behavior of the fundamental gap with composition for this compound was found to be 0.416 ± 0.06. The thermal characteristics of grown Cd1-xZnxSe alloys were systematically studied. The thermal diffusivity and effusivity of the crystals under investigation were experimentally determined, allowing the calculation of the thermal conductivity. We applied the semi-empirical model that Sadao Adachi developed to analyze the results. Thanks to that, it was possible to estimate the contribution arising from chemical disorder to the crystal's total resistivity.